Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Basis
- Universal general purpose resin
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Properties
• unfilled
• extreme low viscosity
• high filler content possible
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Applications
Bonding resin for fillers
Bonding resin for backfillings- Processing Instructions
- The temperature of material and processing should be between 18 and 25° C.
- The mixing of resin and hardener should be made intensively and if possible without any bubbles at room temperature.
- We recommend a post curing with a temperature rise of about 10°C/hour. Difficult geometries should be supported during the curing cycle. Afterwards the part should be cooled down at about 20°C/hour.
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Compressive Strength | 80 ± 5 | MPa | EN ISO 604 |
| Shore hardness | 82 ± 3 | Shore D | DIN ISO 7619-1 |
| Viscosity (25°C) | 200 ± 50 | mPa.s | — |
| Flexural elongation at break | 5.6 ± 0.5 | % | EN ISO 178 |
| Density (20°C) | 1,0 ± 0,02 | g/cm3 | — |
| Flexural modulus | 2900 ± 200 | MPa | EN ISO 178 |
| Pot Life (200g/20°C) | 45 - 55 | minutes | — |
| Flexural strength | 95 ± 5 | MPa | EN ISO 178 |
| Curing time at RT | 14 - 16 | Hrs | — |
| Heat resistance (HDT) | 58 ± 3 | °C | DIN EN ISO 75 B |
| Impact resistance (Charpy) | 48 ± 10 | kJ/m2 | EN ISO 179 |
Storage & Handling
- Storing
At appropriate storage 18-25°C. Occuring crystallization due to disadvantageous storage conditions can be made return by warming up the material at approx. 60° C for some hours. Opened containers should be closed immediately after use and be protected against moisture. This material should be used up as soon as possible.