Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Properties
unfilled
low viscosity
high strength
fast curing
Applications & Uses
- Applications
- Cure Method
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Applications
Laminating resin for fabrics
Vehicle construction
Aircraft construction- Processing Instructions
- The temperature of material and processing should be between 18 and 25° C.
- The mixing of resin and hardener should be made intensively and if possible without any bubbles at room temperature.
- We recommend a post curing with a temperature rise of about 10°C/hour. Difficult geometries should be supported during the curing cycle. Afterwards the part should be cooled down at about 20°C/hour.
Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
Shore hardness | 86 ± 2 | Shore D | DIN ISO 7619-1 |
Viscosity (25°C) | 700 ± 100 | mPa.s | — |
Coefficient of thermal expansion | 10-6K-1 | 10-6K-1 | — |
Density (20°C) | 1,12 ± 0,02 | g/cm3 | — |
Compressive Strength | 100 ± 10 | MPa | EN ISO 604 |
Pot Life (200g/20°C) | 20 - 25 | minutes | — |
Flexural elongation at break | 7.3 ± 0.2 | % | EN ISO 178 |
Curing time at RT | 6-8 | Hrs | — |
Flexural modulus | MPa | MPa | EN ISO 178 |
Post Curing | 6 - 8 ( 50 - 60) | Time in h (Temperature in °C) | — |
Post Curing | 3 - 5 ( 80 - 90) | Time in h (Temperature in °C) | — |
Heat resistance (HDT) | °C | °C | — |
Storage & Handling
- Storing
- At appropriate storage 18-25°C.
- Occuring crystallization due to disadvantageous storage conditions can be made return by warming up the material at approx. 60° C for some hours.
- Opened containers should be closed immediately after use and be protected against moisture. This material should be used up as soon as possible.
- Shelf life is indicated on the labels