Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Properties
cures tack free
Applications & Uses
- Applications
- Cure Method
- Plastics & Elastomers End Uses
- Processing Instructions
- The temperature of material and processing should be between 18 and 25° C.
- The mixing of resin and hardener should be made intensively and if possible without any bubbles at room temperature.
- We recommend a post curing with a temperature rise of about 10°C/hour. Difficult geometries should be supported during the curing cycle. Afterwards the part should be cooled down at about 20°C/hour.
Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
Shore hardness | 87 ± 3 | Shore D | DIN ISO 7619-1 |
Viscosity (25°C) | 600 ± 75 | mPa.s | - |
Compressive Strength 0,75 % proof stress | 91 ± 5 | MPa | - |
Density (20°C) | 1,12 ± 0,03 | g/cm3 | - |
Flexural elongation at break | 6.7 ± 0.2 | % | EN ISO 178 |
Pot Life (200g/20°C) | 18 - 22 | minutes | - |
Flexural modulus | 3320 ± 250 | MPa | EN ISO 178 |
Curing time at RT | 16 - 24 | Hrs | - |
Flexural strength | 123 ± 10 | MPa | EN ISO 178 |
Post Curing | 4 ( 120) | Time in h (Temperature in °C) | - |
Glass transition temperature TG | 83 | °C | - |
Heat resistance (HDT) | 91 ± 3 | °C | DIN EN ISO 75 B |
Impact resistance (Charpy) | 51 ± 19 | kJ/m2 | EN ISO 179 |
Storage & Handling
- Storing
- At appropriate storage 18-25°C.
- Occuring crystallization due to disadvantageous storage conditions can be made return by warming up the material at approx. 60° C for some hours.
- Opened containers should be closed immediately after use and be protected against moisture. This material should be used up as soon as possible.