Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Basis
- Slow curing PU-casting system
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Properties
unfilled
slow curing
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Applications
Sheet metal forming
Foundry pattern
Negatives
fixtures- Processing Instructions
- Material- and processing temperature: between 18 - 25 °C.
- Close containers after use.
- Seal porous mold surfaces first (ebalta mold sealer).
- For optimum mold releasing we recommend a special release agent (like T1-1), which can be applied easily with a brush or be sprayed. Releasing of the mold 2-3 times, evaporate for about 20 min. after each releasing.
Mixing ratio resin/hardener according to instructions.
- Stirring rods etc. with residual resin can be easily cleaned with ebaclean.
Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
Wear jet test | 138 | W(V/t) [mm³/min] | — |
Viscosity (25°C) | 500 ± 100 | mPa.s | — |
Coefficient of linear expansion (20 - 50 °C) | 108 | 10-6K-1 | — |
Density (20°C) | 1,2 ± 0,03 | g/cm3 | — |
Compressive Strength | 80 ± 8 | MPa | EN ISO 604 |
Pot Life (200g/20°C) | 45 - 60 | minutes | — |
Elongation | 10 ± 3 | % | — |
Curing time at RT | 16 - 24 | Hrs | — |
Flexural elongation at break | 7.4 ± 0.4 | % | EN ISO 178 |
Flexural modulus | 2250 ± 250 | MPa | EN ISO 178 |
Flexural strength | 110 ± 10 | MPa | EN ISO 178 |
Heat resistance (HDT) | 76 ± 3 | °C | DIN EN ISO 75 B |
Impact resistance (Charpy) | 58 ± 8 | kJ/m2 | EN ISO 179 |
Shore hardness | 82 ± 3 | Shore D | DIN ISO 7619-1 |
Tensile strength | 50 ± 5 | kN/m | — |
Packaging & Availability
- Packages
Comp. A GM 708 8,000 kg / 16,000 kg / 50,000 kg Comp. B PUR 4 Comp. B 6,000 kg
Storage & Handling
- Storing
- Storage at room temperature 18-25 °C.
- Opened containers should be closed immediately after use and should be used up as soon as possible.