Flexible casting resin
Features & Benefits
- Materials Features
- Properties
shore A hardness 45
excellent flow properties
transparent
easily dyeable
odorless
free of mercury
high tear strength
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Applications
Prototypes with rubber-like properties
Flexible parts- Processing Instructions
Material- and processing temperature between 18°C and 25°C.
Mixing ratio resin and hardener according instructions.
Mold temperature for fabircation of vacuum casting parts: 70°C
Final properties reached after 7 days at room temperature or 4 hrs. post curing at 70°C
Any resin residues at mixing rods, can be removed with ebalta cleaning Agent.
To accelerate use our Accelerator 08.
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Tensile strength | 3.5 ± 0.4 | MPa | ISO 37 |
| Viscosity (25°C) | 1500 ± 200 | mPa.s | — |
| Elongation at break / test piece type 2 | 1450 ± 200 | % | ISO 37 |
| Density (20°C) | 1,04 ± 0,02 | g/cm3 | — |
| Shore hardness | 45 ± 3 | Shore A | DIN ISO 7619-1 |
| Pot Life (200g/20°C) | 25 - 35 | minutes | — |
| Tear resistance arch shaped test piece with incision 1 mm | 7.6 ± 0.5 | kN/m | DIN ISO 34-1 |
| Curing time at RT | 12-15 | Hrs | — |
| Curing Time (70°C) | 3 | Hrs | — |
Packaging & Availability
- Sales Units (Packages)
Units
Comp. A GM 956 Comp. A (Isocyanate) 1,000 kg / 5,000 kg
Comp. B GM 956-45 Comp. B (polyol)e) 1,800 kg
Storage & Handling
- Storing
Storage at room temperature 18-25 °C.
Opened containers should be closed immediately after use and should be used up as soon as possible.
Shelf life: see labels