Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Electrical Properties
- Processing Information (Injection Molding)
- Rheological Properties
Value | Units | Test Method / Conditions | |
Yield Stress (at 50mm/min) | 48.0 | MPa | ISO 527-1,-2 |
Tensile Strain at Break (at 50mm/min) | min. 15 | % | Acc. ISO 527-1,-2 |
Tensile Modulus (at 1mm/min) | 2500.0 | MPa | ISO 527-1,-2 |
Flexural Strength (at 2 mm/min) | 71.0 | MPa | ISO 178 |
Flexural Modulus (at 2 mm/min) | 2400.0 | MPa | ISO 178 |
Izod Notched Impact Strength (at 23°C) | 18.0 | kJ/m² | ISO 180-1A |
Izod Notched Impact Strength (at -30°C) | 10.0 | kJ/m² | ISO 180-1A |
Yield Strain (at 50mm/min) | 2.4 | % | ISO 527-1,-2 |
Charpy Impact Strength (at 23°C) | 180.0 | kJ/m² | ISO 179-1eU |
Charpy Impact Strength (at -30°C) | 90.0 | kJ/m² | ISO 179-1eU |
Charpy Notched Impact Strength (at 23°C) | 20.0 | kJ/m² | ISO 179-1eA |
Charpy Notched Impact Strength (at -30°C) | 11.0 | kJ/m² | ISO 179-1eA |
Ball Indentation Hardness | 105.0 | N/mm² | ISO 2039-1 |
Vicat Softening Temperature (at 50N, 50ºC/h) | 96.0 | ºC | ISO 306 |
Value | Units | Test Method / Conditions | |
Temperature of Deflection Under Load (at 1.80 MPa) | 92.0 | ºC | ISO 75-1,-2 |
Temperature of Deflection Under Load (at 0.45 MPa) | 96.0 | ºC | ISO 75-1,-2 |
Burning Behavior (at 1.6 mm) | HB | Class | UL 94 |
Coefficient of Linear Thermal Expansion (Parallel, 23 - 55°C) | 0.9 | 10^{-4} /K | ISO 11359 -1, -2 |
Burning Rate (US-FMVSS, 2.0 mm) | 50.0 | mm/min | ISO 3795 |
Glow Wire Test (GWFI, 2.0 mm) | 650.0 | ºC | IEC 60695-2-12 |
Value | Units | Test Method / Conditions | |
Density | 1.05 | g/cm³ | ISO 1183 |
Value | Units | Test Method / Conditions | |
Relative Permittivity (at 100MHz) | 3.1 | — | IEC 60250 |
Relative Permittivity (at 1MHz) | 2.9 | — | IEC 60250 |
Dissipation Factor (at 100 MHz) | 60.0 | 10^{-4} | IEC 60250 |
Dissipation Factor (at 1 MHz) | 80.0 | 10^{-4} | IEC 60250 |
Volume Resistivity | 10000000000000.0 | Ohm·m | IEC 60093 |
Surface Resistivity | 1.0e+15 | Ohm | IEC 60093 |
Electric Strength | 33.0 | kV/mm | IEC 60243-1 |
Comparative Tracking Index | 600.0 | Rating | IEC 60112 |
Value | Units | Test Method / Conditions | |
Injection Molding-Melt Temperature | 240.0 | ºC | ISO 294 |
Injection Molding-Mold Temperature | 70.0 | ºC | ISO 294 |
Injection Molding-Injection Velocity | 240.0 | mm/s | ISO 294 |
Value | Units | Test Method / Conditions | |
Molding Shrinkage (Normal, 60x60x2) | 0.4 - 0.7 | % | ISO 294-4 |
Melt Volume-Flow Rate (at 220°C, 10kg) | 12.0 | cm³/(10 min) | ISO 1133 |
Molding Shrinkage (Parallel, 60x60x2) | 0.4 - 0.7 | % | ISO 294-4 |