Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Other Properties
- Mechanical Properties (TPE)
- Rheological Properties
Value | Units | Test Method / Conditions | |
Yield Stress | 15 | MPa | ISO 527-1/-2 |
Yield Strain | 22 | % | ISO 527-1/-2 |
Nominal Strain at Break | >50 | % | ISO 527-1/-2 |
Charpy Notched Impact Strength (at +23°C) | N | kJ/m² | ISO 179/1eA |
Izod Notched Impact Strength (at +23°C) | N | kJ/m² | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Melting Temperature (10°C/min) | 200 | °C | ISO 11357-1/-3 |
Temperature of Deflection Under Load (0.45 MPa) | 85 | °C | ISO 75-1/-2 |
Vicat Softening Temperature (50°C/h 50N) | 90 | °C | ISO 306 |
Burning Behaviour (at 1.5 mm Nominal Thickness) | UL V-2 | class | IEC 60695-11-10 |
Relative Temperature Index (Electrical, 1.5 mm) | 50 | °C | UL746B |
Relative Temperature Index (with impact, 1.5 mm) | 50 | °C | UL746B |
Relative Temperature Index (without impact, 1.5 mm) | 50 | °C | UL746B |
Value | Units | Test Method / Conditions | |
Relative Permittivity (100Hz) | 5.2 | — | IEC 62631-2-1 |
Dissipation Factor (100 Hz) | 0.02 | E-4 | IEC 62631-2-1 |
Volume Resistivity | >1E13 | Ohm*m | IEC 62631-3-1 |
Electric Strength | 20 | kV/mm | IEC 60243-1 |
Comparative Tracking Index | 600 | V | IEC 60112 |
Value | Units | Test Method / Conditions | |
Water Absorption | 0.6 | % | Sim. to ISO 62 |
Humidity Absorption | 0.25 | % | Sim. to ISO 62 |
Density | 1280 | kg/m³ | ISO 1183 |
Value | Units | Test Method / Conditions | |
Tensile Modulus | 250 | MPa | ISO 527-1/-2 |
Stress at 10% strain | 13 | MPa | ISO 527-1/-2 |
Stress at 100% strain | 17.5 | MPa | ISO 527-1/-2 |
Stress at Break | 27 | MPa | ISO 527-1/-2 |
Nominal Strain at Break | 375 | % | ISO 527-1/-2 |
Shore D Hardness (3s) | 55 | — | ISO 868 |
Shore D Hardness (15s) | 55 | — | ISO 868 |
Value | Units | Test Method / Conditions | |
Melt Volume-Flow Rate (at 230 / * °C, 2.16 / * kg) | 15 | cm³/10min | ISO 1133 |
Melt Flow Index (at 230 °C, 2.16 kg) | 14.4 | g/10min | ISO 1133 |
Molding Shrinkage (parallel) | 1.35 | % | Sim. to ISO 294-4 |
Molding Shrinkage (normal) | 1.35 | % | Sim. to ISO 294-4 |
Regulatory & Compliance
- Certifications & Compliance
- OEM Specifications
- OEM Standards
- Quality Standards
Technical Details & Test Data
- Chemical Resistance
Chemical Type Chemical Name Resistance Other Acetic acid (10% by mass) at 23°C resistant Ketones Acetone at 23°C resistant Other Ammonium hydroxide (10% by mass) at 23°C limited resistant, tests necessary to verify Other ASTM 1 at 23°C resistant Other ASTM 3 at 23°C resistant Other Brake fluids (DOT 3/4) at 23°C not resistant Other Calcium chloride (10% by mass) at 23°C limited resistant, tests necessary to verify Other Chloroform at 23°C not resistant Ethers Diethyl ether at 23°C limited resistant, tests necessary to verify Alcohols Ethanol at 23°C limited resistant, tests necessary to verify Other Ethyl Acetate at 23°C limited resistant, tests necessary to verify Other Fuel; Diesel at 85°C resistant Other Hydrochloric acid (10% by mass) at 23°C resistant Other Hydrogen peroxide (30% by mass) at 23°C limited resistant, tests necessary to verify Other Nitric acid (10% by mass) at 23°C resistant Other Phosphoric acid (10% by mass) at 23°C resistant Other Sodium hydroxide (10% by mass) at 23°C resistant Other Sulfuric acid (30% by mass) at 23°C resistant Other Tetrachloroethylene at 23°C limited resistant, tests necessary to verify Hydrocarbons Toluene at 23°C resistant Other Transformer oil at 23°C not resistant Other Trichloroethylene at 23°C not resistant Other Water at 23°C resistant Other Zinc chloride (10% by mass) at 23°C resistant