1. Mix at room temperature, 100 grams of Part-A with 100 grams of Part-B and vacuum degas.
2. Cure as recommended to achieve the desired properties.
3. Typical cured properties were determined using recommended cure schedule.
4. Some difference in properties may occur with the alternate or other cure schedules.- Industrial Usage
These materials are intended for industrial use only, and the practices of good housekeeping, safety and cleanliness should be followed before, during and after use.
Properties
- Component A
- Typical Properties
- Component B
- Typical Cured Properties
| Value | Units | Test Method / Conditions | |
| Resin Viscocity (at 25°C) | 30000 - 40000 | cPs | — |
| Value | Units | Test Method / Conditions | |
| Mix Ratio (By Weight, Part A/Part B) | 100/100 | — | — |
| MIx Viscocity (at 25°C) | 35000 - 45000 | cPs | — |
| Pot Life (at 25°C, 100g) | 45 - 60 | minutes | — |
| Recommended Cure (at 65°C) | 2 | hours | — |
| Alternate Cure (at 25°C) | 48 | hours | — |
| Value | Units | Test Method / Conditions | |
| Hardner Viscocity (at 25°C) | 35000 - 45000 | cPs | — |
| Value | Units | Test Method / Conditions | |
| Specific Gravity | 1.35 | — | — |
| Hardness | 78 | Shore D | — |
| Lap Shear Strength to Aluminum (at -253°C) | 2400 | psi | — |
| Lap Shear Strength to Aluminum (at -73°C) | 3000 | psi | — |
| Lap Shear Strength to Aluminum (at -25°C) | 3200 | psi | — |
| Lap Shear Strength to Aluminum (at -82°C) | 500 | psi | — |
| Lap Shear Strength to Aluminum (after 7 days Immersed in water at 100°C) | 2300 | psi | — |
| Lap Shear Strength to Aluminum (after 7 days Immersed in Isopropanol at room Temp) | 3290 | psi | — |
| T-peel Strength to Aluminum | 24 | pli | — |
| Service Temperature Range | 55 to 150 | °C | — |
| Glass Transition Temperature (Tg) | 75 | °C | — |
| Coeflicient of Linear Thermal Expansion (at -55°C to 25°C) | 77 | 10^-6/°C | — |
| Coeflicient of Linear Thermal Expansion (at 25°C to 90°C) | 160 | 10^-6/°C | — |
| Dielectric Strength | 410 | Volts/mil | — |
| Dielectric Constant (at 1 kHz) | 4.28 | — | — |
| Dissipation Factor (at 1 kHz) | 0.4 | — | — |
| Volume Resistivity | 3x10^13 | Ω-cm | — |
Safety & Health
- Warning
Although the system contains low volatility materials, care should be taken in handling. Adequate ventilation of workplace and ovens is essential. These materials may cause injury to the skin following prolonged or repeated contact and dermatitis in susceptible individuals. In case of skin contact, wash thoroughly with soap and water. For eyes, flush immediately with plenty of water for at least 10 minutes and seek medical attention.
Storage & Handling
- Shelf Life
The shelf life of these materials is greater than one year when stored in unopened containers at an average temperature of 25°C.