- The material absorbs only little moisture. Therefore dimensions and properties of parts are nearly unaffected through ambient conditions.
- The process temperatures should be in the range of 240-270°C. Pigmentation may affect values.
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Application Information
The melting point of VESTAMID® DX9304 BK E70238, about 35 °C higher than PA 11 and PA 12 compounds, allows higher temperatures in use. The compound is especially suitable for the extrusion of tubing systems that are exposed to high burst pressures at high service temperatures, e.g. hydraulic clutch lines.
Properties
- Color
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Test Specimen Production
- Rheological Properties
- Burn Testing Properties
Value | Units | Test Method / Conditions | |
Tensile Modulus (dry) | 268000 | psi | ISO 527 |
Tensile Modulus (cond.) | 174000 | psi | ISO 527 |
Tensile Strength (dry) | 7250 | psi | ISO 527 |
Yield Stress (dry) | 7250 | psi | ISO 527 |
Yield Stress (cond.) | 5950 | psi | ISO 527 |
Yield Strain (dry) | 5 | % | ISO 527 |
Yield Strain (cond.) | 20 | % | ISO 527 |
Stress at Break (dry) | 6240 | psi | ISO 527 |
Nominal Strain at Break (ɛtb, dry) | 41 | % | ISO 527 |
Nominal Strain at Break (ɛtb, cond.) | min. 50 | % | ISO 527 |
Charpy Notched Impact Strength (+23°C, dry) | 19 | ftlb/in² | ISO 179/1eA |
Charpy Notched Impact Strength (+23°C, cond.) | 45.2 | ftlb/in² | ISO 179/1eA |
Charpy Notched Impact Strength (-30°C, dry) | 14.3 | ftlb/in² | ISO 179/1eA |
Charpy Notched Impact Strength (-30°C, cond.) | 8.56 | ftlb/in² | ISO 179/1eA |
Flexural Modulus (23°C, dry) | 264000 | psi | ISO 178 |
Flexural Modulus (23°C, cond.) | 152000 | psi | ISO 178 |
Flexural Stress at Conv. Deflection (23°C, dry) | 8410 | psi | ISO 178 |
Flexural Stress at Conv. Deflection (23°C, cond.) | 4640 | psi | ISO 178 |
Flexural Strength (23°C, dry) | 10400 | psi | ISO 178 |
Flexural Strength (23°C, cond.) | 6380 | psi | ISO 178 |
Flexural Strain at Flexural Strength (23°C, dry) | 7 | % | ISO 178 |
Flexural Strain at Flexural Strength (23°C, cond.) | 8 | % | ISO 178 |
Value | Units | Test Method / Conditions | |
Density (dry) | 1.04 | g/cm³ | ISO 1183 |
Density (cond.) | 1.04 | g/cm³ | ISO 1183 |
Water Absorption (dry) | 2.7 | % | Sim. to ISO 62 |
Humidity Absorption (dry) | 1.3 | % | Sim. to ISO 62 |
Shore D Hardness (dry) | 75(3 sec) | — | ISO 7619-1 |
Shore D Hardness (cond.) | 74(3 sec) | — | ISO 7619-1 |
Value | Units | Test Method / Conditions | |
Melting Temperature (dry) | 415 | °F | ISO 11357-1/-3 |
Temperature of Deflection Under Load A (1.80 Mpa, dry) | 122 | °F | ISO 75-1/-2 |
Temperature of Deflection Under Load B (0.45 Mpa, dry) | 338 | °F | ISO 75-1/-2 |
Vicat Softening Temperature A (10 N, 50 K/h, dry) | 408 | °F | ISO 306 |
Vicat Softening Temperature B (50 N, 50 K/h, dry) | 347 | °F | ISO 306 |
Coefficient of Linear Thermal Expansion (23°C to 55 °C, Parallel, dry) | 8.33e-05 | in/in/°F | ISO 11359-1/-2 |
Value | Units | Test Method / Conditions | |
Volume Resistivity (pV, dry) | 3.2E12 | Ohm*m | IEC 62631-3-1 |
Volume Resistivity (pV, cond.) | 1.8E10 | Ohm*m | IEC 62631-3-1 |
Surface Resistivity (σC, Circular Electrodes, dry) | 1.3E14 | Ohm/sq | IEC 62631-3-2 |
Surface Resistivity (σC, Circular Electrodes, cond.) | 1.4E14 | Ohm/sq | IEC 62631-3-2 |
Relative Permittivity (50Hz, dry) | 4.2 | — | IEC 62631-2-1 |
Relative Permittivity (100Hz, dry) | 4.1 | — | IEC 62631-2-1 |
Relative Permittivity (1MHz, dry) | 3.2 | — | IEC 62631-2-1 |
Dissipation Factor (50Hz, dry) | 690 | E-4 | IEC 62631-2-1 |
Dissipation Factor (100Hz, dry) | 560 | E-4 | IEC 62631-2-1 |
Dissipation Factor (1Mhz, dry) | 310 | E-4 | IEC 62631-2-1 |
Electric Strength (AC, S20/S20, t. 1 mm, dry.) | 991 | kV/in | IEC 60243-1 |
Electric Strength (AC, S20/S20, t. 1 mm, cond.) | 965 | kV/in | IEC 60243-1 |
Comparative Tracking Index (Test Solution A, 50 Drops Value, dry) | 600 | — | IEC 60112 |
Value | Units | Test Method / Conditions | |
Injection Molding - Melt Temperature | 482 | °F | ISO 294 |
Injection Molding - Mold Temperature | 176 | °F | ISO 294 |
Injection Molding - Injection Velocity | 7.87 | in/s | ISO 294 |
Value | Units | Test Method / Conditions | |
Melt Volume Flow Rate (dry, at 536°F, 1lb) | 7 | cm³/10min | ISO 1133 |
Molding Shrinkage (Parallel, dry) | 21 | % | ISO 294-4, 2577 |
Molding Shrinkage (Normal, dry) | 1.2 | % | ISO 294-4, 2577 |
Mold Temperature (dry) | 176 | °F | — |
Melt Temperature (dry) | 500 | °F | — |
Value | Units | Test Method / Conditions | |
Burning Behavior (at 1.5 mm Nominal Thickness) (dry) | HB | class | IEC 60695-11-10 |
Burning Behavior (at Thickness 0.1260 in.) (dry) | HB | class | IEC 60695-11-10 |
Storage & Handling
- Shelf Life
- 2 years
- Storage Conditions
Inside the original and undamaged packaging, the product has a shelf life of at least 2 years when stored in dry rooms at temperatures not exceeding 30°C.