HALOX® 700

HALOX® 700 is a white, non-refractive, corrosion-inhibiting pigment used in protective coatings. It provides extended protection in solvent-based and water-based epoxy and urethane coatings through the combination of zinc and aluminum phosphates. When used in alkyd and acrylic coatings, it is recommended to use it in combination with HALOX® Organic Corrosion Inhibitors for optimal performance.

Brand: HALOX (36 products)

Chemical Family: Phosphates, Zinc Salts

Functions: Corrosion Inhibitor, Pigment

Labeling Claims: Heavy Metal-free

Compatible Polymers & Resins: Alkyds, Epoxies (EP), Polyurethanes (PU)

Synonyms: Zinc(II) Phosphate

Technical Data Sheet
Enhanced TDS

Enhanced TDS

Knowde-enriched technical product data sheet

Identification & Functionality

Features & Benefits

Labeling Claims
CASE Ingredients Features

Applications & Uses

Markets
Applications
Compatible Polymers & Resins
Compatible Substrates & Surfaces
Coating Type
Use Level
5 - 12 %
Recommended Loading Levels

Recommended loading level is 5-12% based on total formula weight.

Applications
  • Mixed Metal Phosphate
  • Alkyds
  • Acrylics
  • Water Based Epoxies
  • Solvent 2K Epoxies
  • Urethanes
  • Solvent 2K Polyurethanes
  • Synergist with other HALOX® Organic Corrosion Inhibitors
  • Water and solvent based paints: alkyd, epoxy and polyurethane coatings.

Properties

Appearance
White Powder
Typical Properties
ValueUnitsTest Method / Conditions
D100 Horibamax. 20microns-
D50 Horiba5 - 7microns-
Density3.09g/ml-
Hegman Grind5.5 - 6.0--
LOI (at 600°C)9.8%-
Oil Absorption36lbs/100 lbs-
pH (10% Slurry by Weight)5.1--

Regulatory & Compliance

Technical Details & Test Data

Heavy Metal Free versus Zinc

Water based Light Industrial DTM Epoxy ASTM B117 @ 168 hours over CRS

CRS     168 Hours  
Sample Panel # DFT Scribe
Creep
ASTM
D 1654
Field
Corrosion
D 610
Field
Blistering
ASTM D
714
Scribe Creep
(mm) AVG of
2 panels
Improvement
vs CTL
Blank 1 4.66 5 10 10 26.375  
2 4.68 4 10 10    
SZP395 1 4.34 5 10 10 6 440%
2 4.4 6 10 10    
700 1 4.58 8 10 10 6.9375 380%
2 4.63 8 10 10    

5% loading level

HALOX® 700 - Heavy Metal Free Versus Zinc

Factors to Consider while Creating Coatings Solutions
  • Combine the inhibitors utilize synergy of multiple mechanisms to achieve desired performance.
    • Inorganic/Flash Rust
    • Inorganic/Inorganic
    • Inorganic/Organic
  • Optimize Solubility of the inhibitor. Synergize short term and long term corrosion inhibitors based on their solubility.
  • Inhibitor Concentration avoid direct weight to weight replacements. Beneficial to optimize usage level.
  • Substrate specific corrosion inhibitor selection can be substrate dependent.

Storage & Handling

Shelf Life
36 Months