Value | Units | Test Method / Conditions | |
Tensile Strength | 108 | MPa | ASTM D 638 |
Flexural Strength | 181 | MPa | ASTM D 790 |
Flexural modulus, 23° | 18000 | MPa | ISO 178 |
Flexural Modulus | 18630 | MPa | ASTM D 790 |
Charpy notched impact strength (+23°) | 5 | kJ/m2 | ISO 179/1eA |
Izod Impact notched (1/8 in) | 39 | J/m | ASTM D 256 |
Rockwell Hardness | 122 | Scale R | ASTM D 785 |
Value | Units | Test Method / Conditions | |
Mold Shrinkage (MD) | 0.002 | mm/mm | ASTM D 955 |
Molding shrinkage - parallel | 0.2 | % | ISO 294-4, 2577 |
Molding shrinkage - normal | 1 | % | ISO 294-4, 2577 |
Mold Shrinkage (TD) | 0.011 | mm/mm | ASTM D 955 |
Density | 1850 | kg/m3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
Coefficient of Thermal Expansion (MD) | 200 | E-6/K | ASTM D 696 |
Deflection Temperature Under Load (264 psi) | 260 | °C | ASTM D 648 |
Temperature of deflection under load (1.80 Mpa) | 260 | °C | ISO 75-1/-2 |
Deflection Temperature Under Load (66 psi) | 265 | °C | ASTM D 648 |
Melting temperature (10°C/min) | 285 | °C | ISO 11357-1/-3 |
Thickness tested | 0.8 | mm | — |
Burning Behavior at thickness | V-0 | class | IEC 60695-11-10 |
Melting Temperature | 285 | °C | ASTM D 3418 |
Value | Units | Test Method / Conditions | |
Dielectric Strength (Short Time) | 16 | kV/mm | ASTM D 149 |
Dielectric Constant (1 MHz) | 5 | - | ASTM D 150 |
Arc Resistance | 115 | s | ASTM D 495 |
Value | Units | Test Method / Conditions | |
Flame rating | V-0 | - | UL 94 |