Identification & Functionality
- Chemical Family
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
- Ready-to-Use Product Features
- Key Attributes
- Flexible and low modulus
- Flame-retardant—meets UL 94V-0
- Convenient 1A:1B volume mix ratio
- Low exotherm
- Good adhesion to a wide variety of substrates including metals, composites, glass, ceramics, and many plastics
- Excellent electrical insulating characteristics
- Non-halogenated flame-retardant fillers
- Solvent-free
- Recommended Preparation
- Clean the substrate with Isopropyl Alcohol, MG #824, so the surface is free of oils, dust, and other residues.
Applications & Uses
- Markets
- Applications
- Compatible Substrates & Surfaces
- Cure Method
Properties
- Flame Rating
- Typical Properties
- Cured Properties
- Uncured Properties
- Cure Instructions
Allow to cure at room temperature for 24 hours, or cure in an oven at one of these time/temperature options:
Temperature 65 °C 80 °C 100 °C Time 2 h 1 h 30 min
| Value | Units | Test Method / Conditions | |
| Mix Ratio | 1:1 | Volume | — |
| Mix Ratio | 1:1 | Weight | — |
| Working Time | 2.5 | h | — |
| Value | Units | Test Method / Conditions | |
| Breakdown Voltage | 48300 | V | — |
| Compressive Strength | 87 | N/mm2 | — |
| CTE (After Tg) | 114 | ppm/˚C | — |
| CTE (Prior Tg) | 142 | ppm/˚C | — |
| Dielectric Strength | 386 | V/mil | — |
| Glass Transition Temperature (Tg) | 50 | °C | — |
| Hardness D | 81 | — | — |
| Intermittent Temperature | 200 | ˚C | — |
| Lap Shear (Aluminum) | 16 | N/mm2 | — |
| Lap Shear (Stainless Steel) | 13 | N/mm2 | — |
| Resistivity | 8.2 x 10¹² | Ω·cm | — |
| Service Temperature Range | -30 to 175 | ˚C | — |
| Tensile Strength | 23 | N/mm2 | — |
| Thermal Conductivity (at 25˚C) | 0.7 | W/(m·K) | — |
| Value | Units | Test Method / Conditions | |
| Mixed Density | 1.6 | g/mL | — |
| Viscosity (at 25 ˚C) ⁽ᵃ⁾ | 8 | Pa·s | — |
| Viscosity (at 25 ˚C) ⁽ᵇ⁾ | 16 | Pa·s | — |
Regulatory & Compliance
- Certifications & Compliance
Technical Details & Test Data
- Mixing
- Scrape settled material free from the bottom and sides of the part A container; stir the contents until homogenous. Use a paint shaker if available.
- Measure 2 parts by volume of the part A and pour into the mixing container. Ensure all contents are transferred by scraping the container.
- Measure 1 part by volume of the part B and pour into the mixing container. Ensure all contents are transferred by scraping the container.
- Thoroughly and gently mix parts A and B together. Avoid introducing air bubbles.
- To de-air, let sit for 15 minutes or put in a vacuum chamber at 25 inHg for 2 minutes.
- If bubbles are present at the top, break them gently with the mixing paddle.
- Pour the mixture into a container holding the components to be protected.
- Close the part A and B containers tightly between uses to prevent skinning.
- Viscosity vs. Temperature
Packaging & Availability
- Available Packaging
Cat. No. Packaging Net Vol. Net Wt. 834FX-450ML 2 Bottle kit 450 mL 728 g 834FX-450ML 2 Can kit 1.7 L 2.75 kg
Storage & Handling
- Shelf Life
- 5 Years
- Storage and Handling
- Store between 16 and 27 ˚C in a dry area, away from sunlight (see SDS).