Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Labeling Claims
- Materials Features
- Product Features
- Good processability and wide processing operating window
- Using conventional fiber spinning machine
- High speed spin continuity of low denier fibers
- Uniform melt flow rate and low gels
- Soft and flexible
- Food contact approved by FDA (FCN No. 1817) and comply to EU10/2011
- Industrial compost certified by BPI in North America and ABA in Australia
- Industrial compost certified by TUV with basis weight 100 gsm
- Renewable content 51% certified by DIN CERTCO
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Typical Properties
- Notes
* Typical properties; not to be construed as specifications
**IV measured at 1.0g/dL in PTM-11 (mixed solvent of Phenol and 1,1,2,2 – Tetrachloroethane 1:1) at 30°C
***Tenacity and elongation obtained from POY 6 dpf with spinning speed 1500 m/min, Screws with L/D ratios of 30:1, Typical melt spinning temperatures are 200-220°C.
Value | Units | Test Method / Conditions | |
Density | 1.26 | g/cm3 | ASTM D792 |
Intrinsic Viscosity** | 1.5 | g/dL | ASTM D4603 |
Melt Flow Rate (190°C, 2.16 kg) | 22.0 | g/10 min | ASTM D1238 |
Melting Temperature | 115.0 | °C | ASTM E794-06 |
Tenacity*** | 3.0 | g/d | ASTM D2256 |
Elonaation*** | 200.0 | % | ASTM D2256 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Regional Availability
Storage & Handling
- Storage Condition
BioPBS™ pellet is dried and packed in aluminum-lined packaging before delivering to customers. The recommended moisture content to prevent potential loss of properties is less than 200 ppm. Typical drying conditions are 80°C for at least 5 hours at a dew point of -40°C or lower. Do not store outdoors. Keep dry at ambient temperature. Avoid humid environment, heat and direct sunlight. Use material within 6 months after delivery date, in order to prevent possible material quality deterioration.