Properties
- Mechanical Properties
- Physical Properties
- Typical Properties
- Electrical Properties
- Impact Properties
- Flame Characteristics
- Wire Coating Extrusion
- Note
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
- ¹⁹ Wire and cable - UL 1581 tested on 2.0mm wire with 0.12mmx20 stranded copper
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 14 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 240 | % | ASTM D638 |
| Flexural Modulus (at 12.5 mm/min, 100 mm span) ¹¹ | 30 | MPa | ASTM D790 |
| Hardness (Shore A, 30S reading) ¹¹ | 79 | — | ASTM D2240 |
| Tensile Stress (Break, 50 mm/min) ¹¹ | 14 | MPa | ISO 527 |
| Tensile Strain (Break, 50 mm/min) ¹¹ | 215 | % | ISO 527 |
| Flexural Modulus (at 12.5 mm/min) ¹¹ | 30 | MPa | ISO 178 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity ¹¹ | 1.02 | — | ASTM D792 |
| Melt Flow Rate (at 250°C, 10.0 kgf) ¹¹ | 11 | g/10 min | ASTM D1238 |
| Value | Units | Test Method / Conditions | |
| Tensile Strength (Break) ¹⁹ | 23 | MPa | UL 1581 |
| Tensile Elongation (Break) ¹⁹ | 310 | % | UL 1581 |
| Tensile Strength (Break, after 7days, at 136°C) ¹⁹ | 21 | MPa | UL 1581 |
| Tensile Elongation (Break, after 7days, at 136°C) ¹⁹ | 246 | % | UL 1581 |
| Heat Deformation (at 121°C, 250g) ¹⁹ | 8 | % | UL 1581 |
| VW-1 ¹⁹ | Pass | — | UL 1581 |
| Value | Units | Test Method / Conditions | |
| Volume Resistivity ¹¹ | 1.40E+16 | Ω.cm | ASTM D257 |
| Relative Permittivity (1 MHz) ¹¹ | 2.6 | — | ASTM D150 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.007 | — | ASTM D150 |
| Dielectric Strength (in oil, at 2mm) ¹¹ | 24.5 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index ¹¹ | 600 | V | IEC 60112 |
| Value | Units | Test Method / Conditions | |
| Brittleness Temperature ¹¹ | max. -40 | °C | ASTM D746 |
| Value | Units | Test Method / Conditions | |
| Oxygen Index (LOI) | 27 | % | ISO 4589 |
| Smoke Density (on 0.5mm plaque, Non-Flame, Ds-max) | 70 | — | ASTM E662 |
| Smoke Density (on 0.5mm plaque, Flame, Ds-max) | 117 | — | ASTM E662 |
| Glow Wire Flammability Index (passes at 960°C) | 3 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 3.0 mm) | 800 | °C | IEC 60695-2-13 |
| Value | Units | Test Method / Conditions | |
| Conductor Pre-heat Temperature | 25 - 120 | °C | — |
| Cooling Water Air Gap | 100 - 200 | mm | — |
| Cross-head Temperature | 220 - 250 | °C | — |
| Die Temperature | 220 - 250 | °C | — |
| Drying Temperature | 75 - 85 | °C | — |
| Drying Time | 5 - 7 | Hrs | — |
| Drying Time (Cumulative) | 12 | Hrs | — |
| Extruder Length/Diameter Ratio (L/D) | 22:1 to 26:1 | — | — |
| Feed Zone Temperature | 180 - 220 | °C | — |
| Head Zone Temperature | 220 - 250 | °C | — |
| Maximum Moisture Content | 0.02 | % | — |
| Melt Temperature | 220 - 250 | °C | — |
| Middle Zone Temperatures | 220 - 250 | °C | — |
| Neck Temperature | 220 - 250 | °C | — |
| Screen Pack | 150 - 100 | — | — |
| Screw Speed | 15 - 85 | rpm | — |
| Water Bath Temperature | 15 - 60 | °C | — |