LNP COLORCOMP™ Compound - D10008ER - SABIC's Specialty

Identification & Functionality

Additives Included: Flame Retardant,
Mold Release Agent
Chemical Family: Polycarbonate (PC)
Polymer Name: Polycarbonate (PC)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics,
Polycarbonates

Features & Benefits

Labeling Claims: No Added PFAS
Materials Features: Easy To Mold,
Excellent Aesthetics,
Flame Retardant,
Good Aesthetics,
Good Mold Release,
Good Moldability,
Good Processability,
Good Surface Appearance,
No Added PFAS,
Non-brominated,
Non-chlorinated,
Unreinforced

Applications & Uses

Markets: Automotive & Transportation,
Consumer Goods,
Electrical & Electronics,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
Interior
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Housewares
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Consumer Goods — Sports & Recreation
Plastics & Elastomers End Uses: Appliances,
Automotive Interior Parts,
Cell Phones,
Commercial Appliance,
Computer Components,
Consumer Applications,
Containers,
Displays,
Electrical/Electronic Applications,
Home Appliances,
Home Decors,
Household Goods,
Personal Accessories,
Sporting Goods,
Tablets
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Color: Custom
Flame Rating: UL 94 V0,
UL 94 V2
Mechanical Properties
Physical Properties
Thermal Properties
Electrical Properties
Optical Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	62	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	68	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	7	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	130	%	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	96	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2340	MPa	ASTM D790
Hardness (Rockwell M) ¹¹	70	—	ASTM D785
Hardness (Rockwell R) ¹¹	118	—	ASTM D785
Taber Abrasion (CS-17, 1 kg) ¹¹	10	mg/1000cy	ASTM D1044

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	1.2	—	ASTM D792
Specific Volume ¹¹	0.83	cm³/g	ASTM D792
Density ¹¹	1.19	g/cm³	ASTM D792
Water Absorption (at 23°C, 24hrs) ¹¹	0.15	%	ASTM D570
Water Absorption (at 23°C, saturated) ¹¹	0.35	%	ASTM D570
Water Absorption (Equilibrium, at 100°C) ¹¹	0.58	%	ASTM D570
Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹	10.5	g/10 min	ASTM D1238
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.5 - 0.7	%	SABIC method

	Value	Units	Test Method / Conditions
Vicat Softening Temperature (Rate B/50) ¹¹	154	°C	ASTM D1525
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹	137	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	132	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 95°C, flow) ¹¹	0.0000684	1/°C	ASTM E831
Specific Heat ¹¹	1.25	J/g-°C	ASTM C351
Thermal Conductivity ¹¹	0.27	W/m-°C	ASTM C177
Relative Temperature Index (Electrical) ᵖ ¹¹	130	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	130	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	130	°C	UL 746B

	Value	Units	Test Method / Conditions
Volume Resistivity ¹¹	min. 1E+17	Ω.cm	ASTM D257
Dielectric Strength (in air, at 3.2mm) ¹¹	14.9	kV/mm	ASTM D149
Relative Permittivity (50/60 Hz) ¹¹	3.17	—	ASTM D150
Relative Permittivity (1 MHz) ¹¹	2.96	—	ASTM D150
Dissipation Factor (at 50/60 Hz) ¹¹	0.0009	—	ASTM D150
Dissipation Factor (at at 1 MHz) ¹¹	0.01	—	ASTM D150
High Voltage Arc Track Rate (PLC) ¹¹	2	PLC Code	UL 746A
Comparative Tracking Index (UL, PLC) ¹¹	2	PLC Code	UL 746A
Hot Wire Ignition (PLC 2) ¹¹	min. 1.5	mm	UL 746A
Hot Wire Ignition (PLC 3) ¹¹	min. 1.1	mm	UL 746A
High Ampere Arc Ignition (PLC 0) ¹¹	min. 1.5	mm	UL 746A
High Ampere Arc Ignition (PLC 1) ¹¹	min. 3	mm	UL 746A
High Ampere Arc Ignition (PLC 2) ¹¹	min. 1.1	mm	UL 746A

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	3204	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	801	J/m	ASTM D256
Tensile Impact Strength (Type S) ¹¹	577	kJ/m²	ASTM D1822
Falling Dart Impact (at 23°C) ¹¹	169	J	ASTM D3029
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹	63	J	ASTM D3763

	Value	Units	Test Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖ	6	mm	UL 94
UL Recognized (94V-2 Flame Class Rating) ᵖ	min. 0.4	mm	UL 94
UV-light (Water exposure/immersion) ᵖ	F2	—	UL 746C

Regulatory & Compliance

Packaging & Availability

LNP™ COLORCOMP™ Compound D10008ER