LNP™ COLORCOMP™ Compound W10009I

Identification & Functionality

Additives Included

Flame Retardant,

Impact Modifier,

Mold Release Agent

Chemical Family

Polyesters

Polymer Name

Polybutylene Terephthalate (PBT)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyesters & Copolyesters

Features & Benefits

Materials Features

Excellent Aesthetics,

Flame Retardant,

Good Aesthetics,

Good Mold Release,

Good Surface Appearance,

High Durability,

High Impact Resistance,

Impact Modified,

Unreinforced

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Interior

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Housewares

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Automotive Applications,

Automotive Interior Parts,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Electrical/Electronic Applications,

Home Appliances,

Home Decoration,

Home Decors,

Household Goods,

Personal Accessories,

Sporting Goods,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Color

Custom

Flame Rating

UL 94 V0

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, 5 mm/min) ¹¹	42	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	4.2	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	1900	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	68	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	1900	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (flow) ᵍ ¹¹	2.3	%	SABIC method
Density ¹¹	1.39	g/cm³	ISO 1183

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	201	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	60	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	125	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	7	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.05	%	—
Melt Temperature ⁷	245 - 260	°C	—
Front - Zone 3 Temperature ⁷	250 - 260	°C	—
Middle - Zone 2 Temperature ⁷	245 - 255	°C	—
Rear - Zone 1 Temperature ⁷	230 - 245	°C	—
Mold Temperature ⁷	80 - 100	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Compliant (94V-0 Flame Class Rating)	1.6	mm	UL 94 by SABIC-IP

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Regional Availability

• Americas
• Asia
• Europe
• North America