Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Impact Properties
- Injection Molding
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Modulus (at 5 mm/min) ¹¹ | 2694 | MPa | ASTM D638 |
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 54 | MPa | ASTM D638 |
Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 49 | MPa | ASTM D638 |
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 7 | % | ASTM D638 |
Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 16 | % | ASTM D638 |
Tensile Modulus (at 1 mm/min) ¹¹ | 2721 | MPa | ISO 527 |
Tensile Stress (Yield, 5 mm/min) ¹¹ | 53 | MPa | ISO 527 |
Tensile Stress (Break, 5 mm/min) ¹¹ | 48 | MPa | ISO 527 |
Tensile Strain (Yield, 5 mm/min) ¹¹ | 6.9 | % | ISO 527 |
Tensile Strain (Break, 5 mm/min) ¹¹ | 14.8 | % | ISO 527 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2640 | MPa | ASTM D790 |
Flexural Modulus (at 2 mm/min) ¹¹ | 2619 | MPa | ISO 178 |
Flexural Stress ¹¹ | 88 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Density ¹¹ | 1.36 | g/cm³ | ASTM D792 |
Specific Gravity ¹¹ | 1.36 | — | ASTM D792 |
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 2.3 | % | ASTM D955 |
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 2.4 | % | ASTM D955 |
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.58 | % | ASTM D570 |
Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.05 | % | ISO 62 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 65 | °C | ASTM D648 |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 155 | °C | ASTM D648 |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 68 | °C | ISO 75/Af |
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 143 | °C | ISO 75/Bf |
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹ | 0.00009 | 1/°C | ASTM D696 |
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹ | 0.00009 | 1/°C | ASTM D696 |
Value | Units | Test Method / Conditions | |
Izod Impact (Notched, at 23°C) ¹¹ | 39 | J/m | ASTM D256 |
Izod Impact (Unnotched, at 23°C) ¹¹ | 1450 | J/m | ASTM D4812 |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 5.4 | kJ/m² | ISO 180/1A |
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 86.7 | kJ/m² | ISO 180/1U |
Multi-Axial Impact ¹¹ | 50.8 | J | ASTM D3763 |
Multi-Axial Impact ¹¹ | 38.6 | J | ISO 6603 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 121 | °C | — |
Drying Time (Cumulative) ⁷ | 4 | Hrs | — |
Melt Temperature ⁷ | 237 - 265 | °C | — |
Front - Zone 3 Temperature ⁷ | 260 - 271 | °C | — |
Middle - Zone 2 Temperature ⁷ | 243 - 254 | °C | — |
Rear - Zone 1 Temperature ⁷ | 221 - 232 | °C | — |
Mold Temperature ⁷ | 82 - 98 | °C | — |
Back Pressure ⁷ | 0.17 - 0.34 | MPa | — |
Screw Speed ⁷ | 30 - 60 | rpm | — |
Maximum Moisture Content ⁷ | 0.05 | % | — |
Packaging & Availability
- Regional Availability