LNP™ ELCRIN™ 610009UXiQ

1 of 65 products in this brand
SABIC's Specialties Business LNP ELCRIN 610009UXiQ compound is based on Polycarbonate / Polybutylene Terephthalate (PC/PBT) blend, utilizing ELCRIN iQ upcycling technology containing minimum 19% Post-Consumer Recycling (PCR) weight content. Added features of this grade include: Flame Retardant, UL746C F1 Rating, UL94 V0 and 5VA Flame Rating, UV Resistant, Impact Modified, Excellent Chemical Resistance. This is a good candidate for applications in the electrical industry including bobbins, switches, and enclosures.

Polymer Name: PC/PBT Alloy

Labeling Claims: Contains PCR Resin, Recyclable, Recycled, Sustainable

Processing Methods: Extrusion, Injection Molding

Density: 1340.0 - 1340.0 kg/m³

Melt Flow Index: 9.3 - 9.3 g/10 min

Technical Data Sheet

Popular SABIC's Specialties Business Products

View All SABIC's Specialties Business Products

Knowde Enhanced TDS

Identification & Functionality

Additives Included

Flame Retardant,

Impact Modifier,

UV Stabilizer

Polymer Name

PC/PBT Alloy

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Recycled Polymers

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Features & Benefits

Labeling Claims

Contains PCR Resin,

Recyclable,

Recycled,

Sustainable

Materials Features

Chemical Resistant,

Flame Retardant,

Good UV Stability,

Good Weather Stability,

High Impact Resistance,

Impact Modified,

Non-chlorinated,

Recyclable,

UV Resistant,

UV Stabilized,

Unreinforced

Value Proposition Compared To Fossil Based PBT Compounds
  • Reduced carbon, energy footprint
  • Improved social impact
  • Similar mechanical properties & color space
  • Drop-in solution for existing tools
  • REACH, RoHS and EPEAT compliant
  • SABIC LNP Health care policy compliance. May comply with regional food contact regulations .

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics,

Industrial,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Interior

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Industrial — Leather & Textiles

Textile Manufacturing

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Housings & Enclosures,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Automotive Applications,

Automotive Interior Parts,

Bobbins,

Cash Dispenser (ATM),

Cell Phones,

Commercial Appliance,

Computer Components,

Connectors,

Consumer Applications,

Containers,

Displays,

Electrical/Electronic Applications,

Enclosure,

Fan Housing,

Personal Accessories,

Sporting Goods,

Switches,

Tablets,

Ticket Machine

Plastics & Elastomers Processing Methods

Extrusion,

Injection Molding

Properties

Flame Rating

UL 746C F1,

UL 94 5VA,

UL 94 HB,

UL 94 V0

Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹48MPaASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹41MPaASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹4.9%ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹74%ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹2000MPaASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹75MPaASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹2100MPaASTM D790
Tensile Stress (Yield, 50 mm/min) ¹¹48MPaISO 527
Tensile Stress (Break, 50 mm/min) ¹¹40MPaISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹4.6%ISO 527
Tensile Strain (Break, 50 mm/min) ¹¹74.8%ISO 527
Tensile Modulus (at 1 mm/min) ¹¹2190MPaISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹73MPaISO 178
Flexural Modulus (at 2 mm/min) ¹¹2050MPaISO 178
Physical Properties
ValueUnitsTest Method / Conditions
Specific Gravity ¹¹1.35—ASTM D792
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹1.1 - 1.4%SABIC method
Melt Flow Rate (at 250°C, 5 kgf) ¹¹9.3g/10 minASTM D1238
Density ¹¹1.34g/cm³ISO 1183
Water Absorption (at 23°C, saturated) ¹¹0.08%ISO 62-1
Moisture Absorption (at 23°C, 50% RH) ¹¹0.08%ISO 62
Melt Volume Rate (at 250°C, 5 kg) ¹¹7cm³/10 minISO 1133
Thermal Properties
ValueUnitsTest Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹95°CASTM D648
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹127°CASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹0.00008161/°CASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹0.00008161/°CISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹0.00009741/°CASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹0.00009741/°CISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹122°CISO 75/Bf
Relative Temperature Index (Electrical) ᵖ ¹¹120°CUL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹120°CUL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹140°CUL 746B
Electrical Properties
ValueUnitsTest Method / Conditions
Comparative Tracking Index (UL, PLC) ᵖ2PLC CodeUL 746A
Arc Resistance (Tungsten, PLC) ᵖ6PLC CodeASTM D495
High Voltage Arc Track Rate (PLC) ᵖ4PLC CodeUL 746A
Hot Wire Ignition (PLC 2) ᵖmin. 3mmUL 746A
Hot Wire Ignition (PLC 3) ᵖmin. 0.63mmUL 746A
Hot Wire Ignition (PLC 4) ᵖmin. 0.46mmUL 746A
High Ampere Arc Ignition (PLC 3) ᵖmin. 1.5mmUL 746A
High Ampere Arc Ignition (PLC 4) ᵖmin. 0.46mmUL 746A
Impact Properties
ValueUnitsTest Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹490J/mASTM D256
Izod Impact (Notched, at -30°C) ¹¹167J/mASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹50JASTM D3763
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹31kJ/m²ISO 180/1A
Izod Impact (Notched, 80*10*4, at -30°C) ¹¹10kJ/m²ISO 180/1A
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹34kJ/m²ISO 179/1eA
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ⁷120°C—
Drying Time ⁷3 - 4Hrs—
Drying Time (Cumulative) ⁷12Hrs—
Maximum Moisture Content ⁷0.02%—
Melt Temperature ⁷250 - 265°C—
Nozzle Temperature ⁷245 - 260°C—
Front - Zone 3 Temperature ⁷250 - 265°C—
Middle - Zone 2 Temperature ⁷245 - 260°C—
Rear - Zone 1 Temperature ⁷240 - 255°C—
Mold Temperature ⁷50 - 75°C—
Back Pressure ⁷0.3 - 0.7MPa—
Screw Speed ⁷50 - 100rpm—
Shot to Cylinder Size ⁷40 - 80%—
Vent Depth ⁷0.025 - 0.038mm—
Flame Characteristics
ValueUnitsTest Method / Conditions
UL Recognized (94-5VA Flame Class Rating) ᵖmin. 2.5mmUL 94
UL Recognized (94V-0 Flame Class Rating) ᵖmin. 0.63mmUL 94
UL Recognized (94HB Flame Class Rating) ᵖ0.46mmUL 94
UV-light (Water exposure/immersion) ᵖF1—UL 746C
Note
  • ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
  • ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
  • ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
  • ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability
  • Americas
  • Asia
  • Europe
  • North America