LNP™ ELCRIN™ WF0061iQ

1 of 65 products in this brand
SABIC's Specialties Business LNP ELCRIN WF0061iQ compound is based on Polybutylene terephthalate (PBT) resin utilizing ELCRIN iQ upcycling technology containing minimum 25% Post-Consumer Recycling (PCR) weight content and 30% glass fiber. Added features of this grade include: Non-Chlorinated, Non-Brominated Flame Retardant, UL94V0 and 5VA Flame Rating, Excellent Chemical Resistance. This is a good candidate for a variety of applications needing a more sustainable FR and PBT solution.

Polymer Name: Polybutylene Terephthalate (PBT)

Additives Included: Flame Retardant

Fillers Included: Glass Fiber

Labeling Claims: Bromine-free, Chlorine-free, Contains PCR Resin, Recyclable, Recycled, Sustainable

Processing Methods: Injection Molding

Density: 1560.0 - 1560.0 kg/m³

Technical Data Sheet

Popular SABIC's Specialties Business Products

View All SABIC's Specialties Business Products

Knowde Enhanced TDS

Identification & Functionality

Additives Included

Flame Retardant

Chemical Family

Polyesters

Fillers Included

Glass Fiber

Polymer Name

Polybutylene Terephthalate (PBT)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Recycled Polymers

Plastics — Engineering & Specialty Polymers

Polyesters & Copolyesters

Features & Benefits

Labeling Claims

Bromine-free,

Chlorine-free,

Contains PCR Resin,

Recyclable,

Recycled,

Sustainable

Materials Features

Chemical Resistant,

Flame Retardant,

High Stiffness,

Non-brominated,

Non-chlorinated,

Recyclable

Value Proposition Compared To Fossil Based PBT Compounds
  • Reduced carbon, energy footprint
  • Improved social impact
  • Similar mechanical properties & color space
  • Drop-in solution for existing tools
  • REACH, RoHS and EPEAT compliant
  • SABIC LNP Health care policy compliance. May comply with regional food contact regulations .

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Interior

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Housewares

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Housings & Enclosures,

Terminal Blocks, Plugs & Sockets

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Automotive Applications,

Automotive Interior Parts,

Cell Phones,

Commercial Appliance,

Computer Components,

Connectors,

Consumer Applications,

Containers,

Displays,

EV Socket,

Electrical/Electronic Applications,

Fan Housing,

Home Appliances,

Home Decoration,

Home Decors,

Household Goods,

Medical/Healthcare Applications,

Personal Accessories,

Sporting Goods,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 5VA,

UL 94 5VB,

UL 94 V0

Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹105MPaASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹105MPaASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹2%ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹2%ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹11000MPaASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹165MPaASTM D790
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹165MPaASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹9600MPaASTM D790
Tensile Stress (Yield, 5 mm/min) ¹¹108MPaISO 527
Tensile Stress (Break, 5 mm/min) ¹¹108MPaISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹2%ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹2%ISO 527
Tensile Modulus (at 1 mm/min) ¹¹11000MPaISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹175MPaISO 178
Flexural Stress (Break, 2 mm/min) ¹¹175MPaISO 178
Flexural Modulus (at 2 mm/min) ¹¹10000MPaISO 178
Physical Properties
ValueUnitsTest Method / Conditions
Specific Gravity ¹¹1.56—ASTM D792
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹0.28%SABIC method
Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹0.57%SABIC method
Density ¹¹1.56g/cm³ISO 1183
Water Absorption (at 23°C, saturated) ¹¹0.23%ISO 62-1
Moisture Absorption (at 23°C, 50% RH) ¹¹0.09%ISO 62
Melt Volume Rate (at 250°C, 5 kg) ¹¹16cm³/10 minISO 1133
Thermal Properties
ValueUnitsTest Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹200°CASTM D648
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹214°CASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹0.0000241/°CASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹0.000081/°CASTM E831
Ball Pressure Test (at 123°C to 127°C) ¹¹Pass—IEC 60695-10-2
Relative Temperature Index (Electrical) ᵖ ¹¹75°CUL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹75°CUL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹75°CUL 746B
Electrical Properties
ValueUnitsTest Method / Conditions
Volume Resistivity ¹¹15Ω.cmASTM D257
Hot Wire Ignition (PLC 1) ᵖ ¹¹min. 0.8mmUL 746A
Hot Wire Ignition (PLC 0) ᵖ ¹¹min. 3mmUL 746A
High Ampere Arc Ignition (PLC 0) ᵖ ¹¹min. 0.8mmUL 746A
Comparative Tracking Index ᵖ ¹¹600VIEC 60112
Impact Properties
ValueUnitsTest Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹570J/mASTM D4812
Izod Impact (Notched, at 23°C) ¹¹72J/mASTM D256
Izod Impact (Notched, at -30°C) ¹¹55J/mASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹6JASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹37kJ/m²ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹7kJ/m²ISO 180/1A
Izod Impact (Notched, 80*10*4, at -30°C) ¹¹6kJ/m²ISO 180/1A
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ⁷110 - 120°C—
Drying Time ⁷2 - 4Hrs—
Maximum Moisture Content ⁷0.02%—
Melt Temperature ⁷245 - 260°C—
Nozzle Temperature ⁷230 - 255°C—
Front - Zone 3 Temperature ⁷240 - 260°C—
Middle - Zone 2 Temperature ⁷235 - 250°C—
Rear - Zone 1 Temperature ⁷230 - 240°C—
Hopper Temperature ⁷40 - 60°C—
Mold Temperature ⁷40 - 100°C—
Flame Characteristics
ValueUnitsTest Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖmin. 0.8mmUL 94
UL Recognized (94-5VB Flame Class Rating) ᵖmin. 3mmUL 94
Glow Wire Ignitability Temperature (at 3.0 mm) ᵖ800°CIEC 60695-2-13
Glow Wire Ignitability Temperature (at 1.5 mm) ᵖ775°CIEC 60695-2-13
Glow Wire Ignitability Temperature (at 0.8 mm) ᵖ750°CIEC 60695-2-13
Glow Wire Flammability Index (at 3 mm) ᵖ960°CIEC 60695-2-12
Glow Wire Flammability Index (at 1.5 mm) ᵖ960°CIEC 60695-2-12
Glow Wire Flammability Index (at 0.8 mm) ᵖ960°CIEC 60695-2-12
Note
  • ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
  • ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
  • ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
  • ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability
  • Americas
  • Asia
  • Europe
  • North America