LNP KONDUIT™ Compound - DTK22 - SABIC's Specialty - PC

Identification & Functionality

Additives Included: Flame Retardant,
Heat Stabilizer,
Mold Release Agent
Chemical Family: Polycarbonate (PC)
Fillers Included: Mineral,
Talc,
Titanium Dioxide
Polymer Name: Polycarbonate (PC)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics,
Polycarbonates

Features & Benefits

Materials Features: Conductive,
Electrically Insulating,
Electrically Isolative,
Flame Retardant,
Good Heat Dissipation,
Good Mold Release,
Good Moldability,
Good Processability,
Heat Stabilized,
Thermally Conductive,
UL Listed

Applications & Uses

Markets: Automotive & Transportation,
Building & Construction,
Consumer Goods,
Electrical & Electronics,
Industrial
Applications: Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
Automotive Lighting
Building & Construction — Building Envelope & Roofing
Glazing & Window Elements
Building & Construction — Building Materials
Interior Fixtures
Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Electrical & Electronics — Devices & Assemblies
Automotive Electronics,
Consumer Electronics,
Displays,
Industrial Automation,
Lighting
Electrical & Electronics — Parts & Components
Housings & Enclosures
Plastics & Elastomers End Uses: Appliances,
Automotive Electronics,
Building Materials,
Camera Applications,
Cell Phones,
Computer Components,
Construction Applications,
Consumer Applications,
Cooling Fan,
Displays,
Electric Vehicles,
Electrical/Electronic Applications,
Electronic Control Unit (ECU),
Flash Light,
Foglamps,
Home Appliances,
Housings,
Industrial Applications,
LEDs,
Lens Folder,
Lighting Applications,
Servomotor,
Tablets,
Thermal Management,
Thermistor,
Wearable Device,
Wireless Communication
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Flame Rating: UL 94 HB
Mechanical Properties
Physical Properties
Thermal Properties
Electrical Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	41	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	5	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	3830	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	79	MPa	ASTM D790
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	77	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	3160	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	42	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	4.1	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	3880	MPa	ISO 527
Flexural Stress (Break, 2 mm/min) ¹¹	81	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	4180	MPa	ISO 178
Impact Strength ¹¹	13 - 48	kJ/m²	ISO R179

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm) ¹¹	127	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2 mm) ¹¹	121	°C	ASTM D648
Coefficient of Thermal Expansion (at 40°C to 120°C, flow) ¹¹	0.000053	1/°C	ASTM E831
Coefficient of Thermal Expansion (at 40°C to 120°C, xflow) ¹¹	0.000085	1/°C	ASTM E831
Thermal Conductivity (through-plane, 60603mm plaque) ¹¹	0.3	W/m-K	ISO 22007-2
Thermal Conductivity (in-plane, 60603mm plaque) ¹¹	1.3	W/m-K	ISO 22007-2
Thermal Conductivity (through-plane, 10103mm sample) ¹¹	0.6	W/m-K	ASTM E1461-07
Thermal Conductivity (in-plane, 25*0.4mm disc) ¹¹	2	W/m-K	ASTM E1461-07
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	128	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	119	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

	Value	Units	Test Method / Conditions
Dielectric Constant (at 1.1 GHz) ¹¹	3.66	—	ASTM ES 7-83
Dissipation Factor (at 1.1 GHz) ¹¹	0.0094	—	ASTM ES 7-83

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	min. 0.5	mm	UL 94
Glow Wire Flammability Index (at 0.8 mm) ᵖ	850	°C	IEC 60695-2-12
Glow Wire Flammability Index (at 1 mm) ᵖ	875	°C	IEC 60695-2-12
Glow Wire Ignitability Temperature (at 0.8 mm) ᵖ	850	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature (at 1.0 mm) ᵖ	850	°C	IEC 60695-2-13

Regulatory & Compliance

Packaging & Availability

LNP™ KONDUIT™ Compound DTK22