Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Break, 5 mm/min) ¹¹ | 105 | MPa | ISO 527 |
Tensile Strain (Break, 5 mm/min) ¹¹ | 1.7 | % | ISO 527 |
Tensile Modulus (at 1 mm/min) ¹¹ | 12000 | MPa | ISO 527 |
Flexural Stress (Yield, at 2 mm/min) ¹¹ | 170 | MPa | ISO 178 |
Flexural Modulus (at 2 mm/min) ¹¹ | 1.10E+04 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.45 | % | ISO 294 |
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.65 | % | ISO 294 |
Density ¹¹ | 1.74 | g/cm³ | ISO 1183 |
Water Absorption (at 23°C, 24hrs) ¹¹ | 0.36 | % | ISO 62-1 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm) ¹¹ | 209 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.0000308 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000477 | 1/°C | ASTM E831 |
Thermal Conductivity (through-plane, 60*60*3mm plaque) ¹¹ | 0.8 | W/m-K | ISO 22007-2 |
Thermal Conductivity (in-plane, 60*60*3mm plaque) ¹¹ | 1.5 | W/m-K | ISO 22007-2 |
Coefficient of Thermal Expansion (at -30°C to 80°C, flow) ¹¹ | 0.0000346 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at -30°C to 80°C, xflow) ¹¹ | 0.0000604 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹ | 0.0000372 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹ | 0.0000734 | 1/°C | ISO 11359-2 |
Thermal Conductivity (through-plane, 80*3mm disc) ¹¹ | 1.1 | W/m-K | ISO 22007-2 |
Thermal Conductivity (in-plane, 80*3mm disc) ¹¹ | 1.3 | W/m-K | ISO 22007-2 |
Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
Ball Pressure Test (at 163°C to 167°C) ¹¹ | Pass | — | IEC 60695-10-2 |
Vicat Softening Temperature (Rate B/120) ¹¹ | 205 | °C | ISO 306 |
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 208 | °C | ISO 75/Bf |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 185 | °C | ISO 75/Af |
Relative Temperature Index (Electrical) ᵖ ¹¹ | 120 | °C | UL 746B |
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 110 | °C | UL 746B |
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 130 | °C | UL 746B |
Value | Units | Test Method / Conditions | |
Surface Resistivity ¹¹ | 1.00E+16 | Ω | ASTM D257 |
Dielectric Strength (in oil, at 1.6mm) ¹¹ | 15.9 | kV/mm | ASTM D149 |
Comparative Tracking Index (UL, PLC) ¹¹ | 0 | PLC Code | UL 746A |
Comparative Tracking Index ʳ ¹¹ | 600 | V | IEC 60112 |
Hot Wire Ignition (PLC 0) ¹¹ | min. 1 | mm | UL 746A |
High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1 | mm | UL 746A |
Value | Units | Test Method / Conditions | |
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 25 | kJ/m² | ISO 180/1U |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 3 | kJ/m² | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 80 | °C | — |
Drying Time ⁷ | 4 | Hrs | — |
Maximum Moisture Content ⁷ | 0.15 - 0.25 | % | — |
Melt Temperature ⁷ | 270 - 295 | °C | — |
Front - Zone 3 Temperature ⁷ | 270 - 290 | °C | — |
Middle - Zone 2 Temperature ⁷ | 270 - 290 | °C | — |
Rear - Zone 1 Temperature ⁷ | 260 - 275 | °C | — |
Mold Temperature ⁷ | 85 - 100 | °C | — |
Back Pressure ⁷ | 0.2 - 0.3 | MPa | — |
Screw Speed ⁷ | 20 - 60 | rpm | — |
Value | Units | Test Method / Conditions | |
UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 1 | mm | UL 94 |
Glow Wire Ignitability Temperature (at 1.0 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature (at 1.5 mm) ᵖ | 775 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature (at 1.6 mm) ᵖ | 775 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature (at 3.0 mm) ᵖ | 800 | °C | IEC 60695-2-13 |
Glow Wire Flammability Index (at 3 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index (at 1.5 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index (at 1 mm) ᵖ | 960 | °C | IEC 60695-2-12 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Regional Availability