LNP™ LUBRICOMP™ Compound DZL24

Identification & Functionality

Additives Included

Lubricant (PTFE)

Chemical Family

Polycarbonate (PC)

Fillers Included

Glass Fiber,

Milled Glass Fiber,

PTFE

Polymer Name

Polycarbonate (PC)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics,

Polycarbonates

Features & Benefits

Materials Features

Dimensional Stability,

Friction Resistant,

Wear Resistant

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Healthcare & Pharma,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Healthcare & Pharma — Medical

Medical Devices & Assemblies

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Home Appliances,

Medical Devices,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, 5 mm/min) ¹¹	36	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	34	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	5.1	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	31.2	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2970	MPa	ISO 527
Flexural Strength (at 2 mm/min) ¹¹	65	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	2840	MPa	ISO 178
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	35	MPa	ASTM D638
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	37	MPa	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	5.1	%	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	26.1	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	3100	MPa	ASTM D638
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹	70	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2980	MPa	ASTM D790

Physical Properties

	Value	Units	Test Method / Conditions
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.13	%	ISO 62
Density ¹¹	1.42	g/cm³	ASTM D792
Specific Gravity ¹¹	1.41	—	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.12	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.3 - 0.6	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.4 - 0.7	%	ASTM D955
Wear Factor Washer ¹¹	61	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Wear Factor Ring ¹¹	4	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.44	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.46	—	ASTM D3702 Modified: Manual

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	140	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	126	°C	ISO 75/Af
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	141	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	127	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000073	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000074	1/°C	ASTM D696

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	12	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	74	kJ/m²	ISO 180/1U
Multi-Axial Impact ¹¹	15	J	ISO 6603
Izod Impact (Notched, at 23°C) ¹¹	140	J/m	ASTM D256
Izod Impact (Unnotched, at 23°C) ¹¹	1120	J/m	ASTM D4812
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	24	J	ASTM D3763

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	305 - 325	°C	—
Front - Zone 3 Temperature ⁷	320 - 330	°C	—
Middle - Zone 2 Temperature ⁷	310 - 320	°C	—
Rear - Zone 1 Temperature ⁷	295 - 305	°C	—
Mold Temperature ⁷	80 - 110	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 