LNP™ LUBRICOMP™ Compound IFL36R

Identification & Functionality

Additives Included

Heat Stabilizer,

Lubricant (PTFE),

Mold Release Agent

Chemical Family

Polyamides

Fillers Included

Glass Fiber,

PTFE

Polymer Name

Polyamide 612 (PA 612)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Friction Resistant,

Good Mold Release,

Heat Stabilized,

High Stiffness,

Wear Resistant

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cash Dispenser (ATM),

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Home Appliances,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Ticket Machine,

Turf Applications,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, 5 mm/min) ¹¹	148	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	147	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	3.3	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	3.4	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	8700	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	200	MPa	ISO 178
Flexural Stress (Break, 2 mm/min) ¹¹	198	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	7300	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Wear Factor Washer ¹¹	9	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.55	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.5	—	ASTM D3702 Modified: Manual
Density ¹¹	1.42	g/cm³	ISO 1183

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000028	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000101	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	197	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	70	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	12	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.12 - 0.2	%	—
Melt Temperature ⁷	270 - 275	°C	—
Front - Zone 3 Temperature ⁷	270 - 280	°C	—
Middle - Zone 2 Temperature ⁷	260 - 270	°C	—
Rear - Zone 1 Temperature ⁷	255 - 265	°C	—
Mold Temperature ⁷	65 - 95	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 