LNP™ LUBRICOMP™ Compound KI001

Identification & Functionality

Additives Included

Heat Stabilizer,

Lubricant (Silicone),

Lubricant (Unspecified)

Fillers Included

Silicone Oil

Polymer Name

Polyacetal Copolymer (POM)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyacetals

Features & Benefits

Materials Features

Friction Resistant,

Heat Stabilized,

Lubricated,

Non-Halogenated,

Unreinforced,

Wear Resistant

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Electronic Components,

Home Appliances,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Modulus (at 1 mm/min) ¹¹	2500	MPa	ISO 527
Tensile Stress (Yield, 5 mm/min) ¹¹	44	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	20	MPa	ISO 527
Flexural Modulus (at 2 mm/min) ¹¹	2000	MPa	ISO 178
Flexural Stress (Yield, at 2 mm/min) ¹¹	65	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (flow) ᵍ ¹¹	2.5	%	SABIC method
Wear Factor Washer ¹¹	66	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.2	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.3	—	ASTM D3702 Modified: Manual
Density ¹¹	1.38	g/cm³	ISO 1183

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000105	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000123	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	87	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	4.2	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	57	kJ/m²	ISO 180/1U

Injection Molding

	Value	Units	Test Method / Conditions
Drying Time ⁷	2 - 3	Hrs	—
Drying Temperature ⁷	80	°C	—
Front - Zone 3 Temperature ⁷	200 - 220	°C	—
Middle - Zone 2 Temperature ⁷	190 - 210	°C	—
Rear - Zone 1 Temperature ⁷	180 - 200	°C	—
Mold Temperature ⁷	80 - 100	°C	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 