SABIC's Specialties Business LNP LUBRICOMP LCL33 compound is based on Polyetheretherketone (PEEK) resin containing 15% carbon fiber, 15% PTFE. Added features of this grade include: Wear Resistant, Electrically Conductive.

Polymer Name: Polyetheretherketone (PEEK)

Processing Methods: Injection Molding

Fillers Included: Carbon Fiber, PTFE

Additives Included: Lubricant (PTFE)

Flexural Modulus: 12960.0 - 12960.0 MPa

Technical Data Sheet

Popular SABIC's Specialties Business Products

View All SABIC's Specialties Business Products

Knowde Enhanced TDS

Identification & Functionality

Additives Included

Lubricant (PTFE)

Chemical Family

Polyether Ether Ketone (PEEK)

Fillers Included

Carbon Fiber,

PTFE

Polymer Name

Polyetheretherketone (PEEK)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Features & Benefits

Materials Features

Electrically Conductive,

Friction Resistant,

High Stiffness,

High Strength,

High Temperature Resistance,

Light Weight,

UL Listed,

Very Good Heat Resistance,

Wear Resistant

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Healthcare & Pharma,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Healthcare & Pharma — Medical

Medical Devices & Assemblies

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Home Appliances,

Personal Accessories,

Pool Covers,

Sporting Goods,

Surgical Devices,

Tablets,

Tarpaulins,

Turf Applications,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹162MPaISO 527
Tensile Stress (Break) ¹¹179MPaASTM D638
Tensile Stress (Break) ¹¹187MPaISO 527
Tensile Strain (Break, 5 mm/min) ¹¹2.9%ISO 527
Tensile Strain (Break) ¹¹1.7%ASTM D638
Tensile Strain (Break) ¹¹1.6%ISO 527
Tensile Modulus (at 1 mm/min) ¹¹14500MPaISO 527
Tensile Modulus (at 50 mm/min) ¹¹16610MPaASTM D638
Flexural Stress (Yield, at 2 mm/min) ¹¹230MPaISO 178
Flexural Stress ¹¹262MPaASTM D790
Flexural Stress ¹¹230MPaISO 178
Flexural Modulus ¹¹12960MPaASTM D790
Flexural Modulus ¹¹11700MPaISO 178
Flexural Strain (Break, at 2 mm/min) ¹¹2.7%ISO 178
Flexural Modulus (at 2 mm/min) ¹¹11700MPaISO 178
Flexural Strain (Break, at 2 mm/min, 80°C) ¹¹2.7%ISO 178
Flexural Strain (Break, at 2 mm/min, 120°C) ¹¹2.7%ISO 178
Flexural Strain (Break, at 2 mm/min, 150°C) ¹¹6%ISO 178
Flexural Strain (Break, at 2 mm/min, 200°C) ¹¹6.3%ISO 178
Flexural Strain (Break, at 2 mm/min, 250°C) ¹¹6.5%ISO 178
Flexural Stress (Yield, at 2 mm/min, 80°C) ¹¹192MPaISO 178
Flexural Stress (Yield, at 2 mm/min, 120°C) ¹¹158MPaISO 178
Flexural Stress (Yield, at 2 mm/min, 150°C) ¹¹100MPaISO 178
Flexural Stress (Yield, at 2 mm/min, 200°C) ¹¹60MPaISO 178
Flexural Stress (Yield, at 2 mm/min, 250°C) ¹¹50MPaISO 178
Flexural Modulus (at 2 mm/min, 80°C) ¹¹10300MPaISO 178
Flexural Modulus (at 2 mm/min, 120°C) ¹¹10200MPaISO 178
Flexural Modulus (at 2 mm/min, 150°C) ¹¹5700MPaISO 178
Flexural Modulus (at 2 mm/min, 200°C) ¹¹3000MPaISO 178
Physical Properties
ValueUnitsTest Method / Conditions
Density ¹¹1.43g/cm³ISO 1183
Density ¹¹1.43g/cm³ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹0.07%ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹0.1 - 0.3%ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹0.1 - 0.3%ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹0.4 - 0.7%ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹0.3 - 0.7%ISO 294
Wear Factor Washer ¹¹1710^-10 in^5-min/ft-lb-hrASTM D3702 Modified: Manual
Dynamic COF ¹¹0.35—ASTM D3702 Modified: Manual
Static COF ¹¹0.28—ASTM D3702 Modified: Manual
Melt Volume Rate (at 400°C, 10.0 kg) ¹¹6 - 8cm³/10 minISO 1133
Thermal Properties
ValueUnitsTest Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2 mm, Unannealed) ¹¹min. 298°CASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹0.00002341/°CASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹0.00002361/°CISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹0.00004141/°CASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹0.00004171/°CISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹min. 300°CISO 75/Af
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹0.00000951/°CISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹0.0000531/°CISO 11359-2
Electrical Properties
ValueUnitsTest Method / Conditions
Surface Resistivity ¹¹1000 - 100000ΩASTM D257
Impact Properties
ValueUnitsTest Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹480J/mASTM D4812
Izod Impact (Notched, at 23°C) ¹¹64J/mASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹9JASTM D3763
Multi-Axial Impact ¹¹9JISO 6603
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹34kJ/m²ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹7kJ/m²ISO 180/1A
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ⁷150°C—
Drying Temperature ⁷120 - 150°C—
Drying Time ⁷4Hrs—
Drying Time ⁷4 - 6Hrs—
Front - Zone 3 Temperature ⁷380 - 400°C—
Front - Zone 3 Temperature ⁷380 - 395°C—
Maximum Moisture Content ⁷0.1%—
Melt Temperature ⁷380 - 390°C—
Middle - Zone 2 Temperature ⁷380 - 400°C—
Middle - Zone 2 Temperature ⁷365 - 375°C—
Rear - Zone 1 Temperature ⁷370 - 380°C—
Rear - Zone 1 Temperature ⁷350 - 360°C—
Mold Temperature ⁷140 - 165°C—
Mold Temperature ⁷175 - 190°C—
Back Pressure ⁷0.3 - 0.7MPa—
Screw Speed ⁷60 - 100rpm—
Note
  • ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
  • ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
  • ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
 