LNP LUBRICOMP™ Compound - LCL33EXQ - SABIC's Specialty

Identification & Functionality

Additives Included: Lubricant (PTFE)
Chemical Family: Polyether Ether Ketone (PEEK)
Fillers Included: Carbon Fiber,
PTFE
Polymer Name: Polyetheretherketone (PEEK)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
High Performance Thermoplastics

Features & Benefits

Materials Features: Easy To Mold,
Electrically Conductive,
Friction Resistant,
Good Moldability,
Good Processability,
High Stiffness,
High Strength,
High Temperature Application,
High Temperature Resistance,
Light Weight,
Very Good Heat Resistance,
Wear Resistant

Applications & Uses

Markets: Building & Construction,
Consumer Goods,
Electrical & Electronics,
Industrial,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Industrial — Chemical & Industrial Manufacturing
Equipment & Parts
Building & Construction — Decorative Materials & Finishes
Artificial Turf
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Lawn & Garden
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Switches & Relays
Consumer Goods — Sports & Recreation
Plastics & Elastomers End Uses: Appliances,
Bearings,
Building Materials,
Cell Phones,
Commercial Appliance,
Computer Components,
Consumer Applications,
Containers,
Displays,
Doors,
Electrical Components,
Electrical/Electronic Applications,
Heavy Vehicles,
Home Appliances,
Personal Accessories,
Pool Covers,
Seal Rings,
Sporting Goods,
Tablets,
Tarpaulins,
Thrust Washer,
Transmission Seal Rings,
Turf Applications,
Valve Parts,
Windows
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Physical Properties
Mechanical Properties
Thermal Properties
Impact Properties
Injection Molding
Note: ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	185	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.8	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	16000	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	277	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	13400	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	181	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.6	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	13960	MPa	ISO 527
Flexural Stress ¹¹	276	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	13530	MPa	ISO 178

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	320	°C	ASTM D648

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	69	J/m	ASTM D256
Izod Impact (Notched, 80104, at 23°C) ¹¹	5	kJ/m²	ISO 180/1A

Packaging & Availability

LNP™ LUBRICOMP™ Compound LCL33EXQ