LNP™ LUBRICOMP™ Compound UFL269SA

Identification & Functionality

Additives Included

Flame Retardant,

Heat Stabilizer,

Lubricant (PTFE),

Mold Release Agent

Chemical Family

Polyamides

Fillers Included

Glass Fiber,

PTFE

Polymer Name

Polyphthalamide (PPA)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Flame Retardant,

Friction Resistant,

Good Mold Release,

Heat Stabilized,

High Stiffness,

High Temperature Resistance,

Very Good Heat Resistance,

Wear Resistant

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics,

Industrial

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Powertrain & UTH

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Electrical & Electronics — Parts & Components

Semiconductor Manufacturing

Plastics & Elastomers End Uses

Appliances,

Automotive Applications,

Automotive Under The Hood,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Displays,

Electrical/Electronic Applications,

Home Appliances,

Industrial Applications,

Semiconductor Applications,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 V0

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break) ¹¹	162	MPa	ASTM D638
Tensile Strain (Break) ¹¹	1.7	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	13650	MPa	ASTM D638
Flexural Stress ¹¹	227	MPa	ASTM D790
Flexural Modulus ¹¹	12820	MPa	ASTM D790

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.71	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.2 - 0.4	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.7 - 0.9	%	ASTM D955
Wear Factor Washer ¹¹	85	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	0.47	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.38	—	ASTM D3702 Modified: Manual

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	273	°C	ASTM D648

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	461	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	85	J/m	ASTM D256

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.15	%	—
Melt Temperature ⁷	315 - 330	°C	—
Front - Zone 3 Temperature ⁷	325 - 340	°C	—
Middle - Zone 2 Temperature ⁷	315 - 325	°C	—
Rear - Zone 1 Temperature ⁷	310 - 320	°C	—
Mold Temperature ⁷	150 - 170	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖ	min. 1.5	mm	UL 94

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

 