LNP™ LUBRICOMP™ Compound YL003

Identification & Functionality

Additives Included

Lubricant (PTFE)

Chemical Family

Polyesters

Fillers Included

PTFE

Polymer Name

Thermoplastic Polyester Elastomer

Technologies

Elastomers

Product Families

Elastomers — Thermoplastic Elastomers

Thermoplastic Polyester Elastomers (TPE-E)

Features & Benefits

Materials Features

Friction Resistant,

Unreinforced,

Wear Resistant

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Garden Equipment,

Home Appliances,

Lawn Equipment,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, 50 mm/min) ¹¹	24	MPa	ISO 527
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	43	MPa	ASTM D638
Tensile Strain (Break, 50 mm/min) ¹¹	455	%	ISO 527
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	14.2	%	ASTM D638
Tensile Modulus (at 1 mm/min) ¹¹	240	MPa	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	180	MPa	ISO 527
Tensile Modulus (at 50 mm/min) ¹¹	230	MPa	ASTM D638
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	230	MPa	ASTM D790
Flexural Stress (Yield, at 2 mm/min) ¹¹	12	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	230	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	220	MPa	ISO 178
Tensile Stress (Yield, 5 mm/min) ¹¹	14	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	43.5	%	ISO 527

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (flow) ᵍ ¹¹	2.3	%	SABIC method
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1 - 3	%	ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	1.5 - 2.5	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1 - 3	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	1.5 - 2.5	%	ISO 294
Density ¹¹	1.28	g/cm³	ISO 1183
Density ¹¹	1.27	g/cm³	ASTM D792
Specific Gravity ¹¹	1.28	—	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.33	%	ASTM D570
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.47	%	ISO 62

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000172	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000188	1/°C	ASTM D696

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	No break	kJ/m²	ISO 180/1U
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	42	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	21	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	35	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, at 23°C) ¹¹	455	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	312	J/m	ASTM D256
Multi-Axial Impact ¹¹	24	J	ISO 6603
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	25	J	ASTM D3763

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Maximum Moisture Content ⁷	0.1	%	—
Melt Temperature ⁷	215 - 240	°C	—
Front - Zone 3 Temperature ⁷	225 - 240	°C	—
Middle - Zone 2 Temperature ⁷	205 - 215	°C	—
Rear - Zone 1 Temperature ⁷	180 - 195	°C	—
Mold Temperature ⁷	25 - 55	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Packaging & Availability