LNP™ LUBRICOMP™ Compound ZFL31XXC

Identification & Functionality

Additives Included

Lubricant (PTFE),

Mold Release Agent

Fillers Included

Glass Fiber,

PTFE

Polymer Name

PPO/PS Alloy

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Features & Benefits

Materials Features

Friction Resistant,

Good Mold Release,

Wear Resistant

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Building Materials

Pipes & Plumbing

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Faucet System Components,

Fittings,

Garden Equipment,

Gears,

Home Appliances,

Lawn Equipment,

Personal Accessories,

Pool Covers,

Pump Parts,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications,

Water Management,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	60	MPa	ASTM D638
Tensile Stress (Break) ¹¹	55	MPa	ASTM D638
Tensile Strain (Break) ¹¹	3.2	%	ASTM D638
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	2.8	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	3650	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	3.5	%	ASTM D638
Flexural Stress ¹¹	89	MPa	ISO 178
Flexural Stress ¹¹	103	MPa	ASTM D790
Flexural Modulus ¹¹	3510	MPa	ASTM D790
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	106	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	3650	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	60	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	2.7	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	3.2	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	3640	MPa	ISO 527
Flexural Modulus (at 2 mm/min) ¹¹	4800	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.2	g/cm³	ASTM D792
Specific Gravity ¹¹	1.21	—	ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.07	%	ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.5 - 0.7	%	ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.6 - 0.8	%	ASTM D955
Wear Factor Washer ¹¹	100	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF ¹¹	4.00E-01	—	ASTM D3702 Modified: Manual
Static COF ¹¹	0.26	—	ASTM D3702 Modified: Manual
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.1	%	ISO 62

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	127	°C	ASTM D648
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	136	°C	ASTM D648
Coefficient of Thermal Expansion (at -30°C to 30°C, flow) ¹¹	0.000066	1/°C	ASTM D696
Coefficient of Thermal Expansion (at -30°C to 30°C, xflow) ¹¹	0.000069	1/°C	ASTM D696
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	134	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	127	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	360	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	80	J/m	ASTM D256
Multi-Axial Impact ¹¹	2	J	ISO 6603
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	12	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	24	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	7	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120	°C	—
Drying Time ⁷	4	Hrs	—
Melt Temperature ⁷	300 - 305	°C	—
Front - Zone 3 Temperature ⁷	300 - 310	°C	—
Middle - Zone 2 Temperature ⁷	290 - 300	°C	—
Rear - Zone 1 Temperature ⁷	275 - 290	°C	—
Mold Temperature ⁷	80 - 110	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	min. 0.8	mm	UL 94

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Regional Availability

• Americas
• Asia
• North America