LNP™ THERMOCOMP™ Compound DX09309

Identification & Functionality

Additives Included

Heat Stabilizer,

Mold Release Agent

Chemical Family

Polycarbonate (PC)

Fillers Included

Mineral,

Titanium Dioxide

Polymer Name

Polycarbonate (PC)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics,

Polycarbonates

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Cost Effective,

Excellent Dielectric Properties,

Good Mold Release,

Heat Stabilized,

No Added PFAS,

Unreinforced

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Interior

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Plastics & Elastomers End Uses

Automotive Applications,

Automotive Interior Parts,

Cell Phones,

Computer Components,

Consumer Applications,

Containers,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Personal Accessories,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	27	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	4.2	%	ASTM D638
Flexural Stress ¹¹	60	MPa	ASTM D790
Flexural Modulus ¹¹	2490	MPa	ASTM D790

Physical Properties

	Value	Units	Test Method / Conditions
Specific Gravity ¹¹	2.24	—	ASTM D792
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.65	%	SABIC method
Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹	0.56	%	SABIC method
Melt Volume Rate (at 280°C, 2.16 kg) ¹¹	20	cm³/10 min	ISO 1133
Melt Volume Rate (at 280°C, 2.16kg) ¹¹	15.7	cm³/10 min	ASTM D1238

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	103	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	97	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000062	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000064	1/°C	ASTM E831

Electrical Properties

	Value	Units	Test Method / Conditions
Dielectric Constant (at 1.1 GHz) ¹¹	8	—	SABIC method
Dissipation Factor (at 1.1 GHz) ¹¹	0.01	—	SABIC method

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	68	J/m	ASTM D256

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	90 - 110	°C	—
Drying Time ⁷	3 - 5	Hrs	—
Melt Temperature ⁷	280 - 320	°C	—
Nozzle Temperature ⁷	280 - 320	°C	—
Front - Zone 3 Temperature ⁷	280 - 320	°C	—
Middle - Zone 2 Temperature ⁷	280 - 320	°C	—
Rear - Zone 1 Temperature ⁷	250 - 280	°C	—
Mold Temperature ⁷	90 - 120	°C	—
Back Pressure ⁷	1 - 5	MPa	—
Screw Speed ⁷	30 - 100	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 