LNP™ THERMOCOMP™ Compound DX11354X

Identification & Functionality

Additives Included

Heat Stabilizer,

Metal Deactivator,

Mold Release Agent

Chemical Family

Polycarbonate (PC)

Fillers Included

Silicone Oil,

Talc

Polymer Name

Polycarbonate (PC)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polycarbonates

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Cost Effective,

Excellent Dielectric Properties,

Good Colorability,

Good Mold Release,

Heat Stabilized,

High Ductility,

High Impact Resistance,

No Added PFAS,

Pigmentable,

Unreinforced

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Interior

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Plastics & Elastomers End Uses

Automotive Interior Parts,

Cell Phones,

Computer Components,

Consumer Applications,

Containers,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Personal Accessories,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding,

Laser Sintering (SLS)

Properties

Color

White

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	55	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	45	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	5	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	70	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	2400	MPa	ASTM D638
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	86	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2380	MPa	ASTM D790
Tensile Stress (Yield, 50 mm/min) ¹¹	54	MPa	ISO 527
Tensile Stress (Break, 50 mm/min) ¹¹	51	MPa	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹	5	%	ISO 527
Tensile Strain (Break, 50 mm/min) ¹¹	84	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2320	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	86	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	2450	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.5 - 0.7	%	ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹	0.5 - 0.7	%	ISO 294
Density ¹¹	1.28	g/cm³	ISO 1183
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.05	%	ISO 62
Melt Volume Rate (at 300°C, 1.2 kg) ¹¹	20	cm³/10 min	ISO 1133

Thermal Properties

	Value	Units	Test Method / Conditions
Vicat Softening Temperature (Rate A/50) ¹¹	136	°C	ASTM D1525
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	121	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000065	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000071	1/°C	ASTM E831
Vicat Softening Temperature (Rate B/50) ¹¹	136	°C	ISO 306
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	117	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	80	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	80	°C	UL 746B

Electrical Properties

	Value	Units	Test Method / Conditions
Volume Resistivity ¹¹	1.00E+16	Ω.cm	ASTM D257
Surface Resistivity ¹¹	1.00E+16	Ω	ASTM D257
Relative Permittivity (1 GHz) ¹¹	3.03	—	ASTM D150
Dissipation Factor (at at 1 GHz) ¹¹	0.0066	—	ASTM D150

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	700	J/m	ASTM D256
Izod Impact (Notched, 80*10*3, at 23°C) ¹¹	60	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	110 - 120	°C	—
Drying Time ⁷	2 - 4	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Melt Temperature ⁷	260 - 280	°C	—
Nozzle Temperature ⁷	255 - 275	°C	—
Front - Zone 3 Temperature ⁷	260 - 280	°C	—
Middle - Zone 2 Temperature ⁷	260 - 280	°C	—
Rear - Zone 1 Temperature ⁷	245 - 265	°C	—
Hopper Temperature ⁷	40 - 60	°C	—
Mold Temperature ⁷	80 - 140	°C	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	min. 1	mm	UL 94

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America