Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Note
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 59 | MPa | ASTM D638 |
Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 11 | % | ASTM D638 |
Tensile Modulus (at 5 mm/min) ¹¹ | 2920 | MPa | ASTM D638 |
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹ | 111 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2890 | MPa | ASTM D790 |
Tensile Stress (Break, 50 mm/min) ¹¹ | 58 | MPa | ISO 527 |
Tensile Strain (Break, 50 mm/min) ¹¹ | 11 | % | ISO 527 |
Tensile Modulus (at 1 mm/min) ¹¹ | 2940 | MPa | ISO 527 |
Flexural Strength (at 2 mm/min) ¹¹ | 112 | MPa | ISO 178 |
Flexural Modulus (at 2 mm/min) ¹¹ | 2880 | MPa | ISO 178 |
Value | Units | Test Method / Conditions | |
Density ¹¹ | 1.29 | g/cm³ | ASTM D792 |
Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.13 | % | ISO 62 |
Melt Volume Rate (at 330°C, 1.2 kg) ¹¹ | 22.8 | cm³/10 min | ISO 1133 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 168 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 155 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000063 | 1/°C | ASTM E831 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000067 | 1/°C | ASTM E831 |
Value | Units | Test Method / Conditions | |
Dielectric Constant (at 1.1 GHz) ¹¹ | 2.95 | — | SABIC method |
Dissipation Factor (at 1.1 GHz) ¹¹ | 0.006 | — | SABIC method |
Value | Units | Test Method / Conditions | |
Izod Impact (Unnotched, at 23°C) ¹¹ | 2160 | J/m | ASTM D4812 |
Izod Impact (Notched, at 23°C) ¹¹ | 61 | J/m | ASTM D256 |
Izod Impact (Unnotched, 80*10*3, at 23°C) ¹¹ | 182 | kJ/m² | ISO 180/1U |
Izod Impact (Notched, 80*10*3, at 23°C) ¹¹ | 7 | kJ/m² | ISO 180/1A |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 135 | °C | — |
Drying Time ⁷ | 4 - 6 | Hrs | — |
Maximum Moisture Content ⁷ | 0.02 | % | — |
Melt Temperature ⁷ | 300 - 345 | °C | — |
Nozzle Temperature ⁷ | 295 - 340 | °C | — |
Front - Zone 3 Temperature ⁷ | 300 - 345 | °C | — |
Middle - Zone 2 Temperature ⁷ | 290 - 335 | °C | — |
Rear - Zone 1 Temperature ⁷ | 280 - 315 | °C | — |
Mold Temperature ⁷ | 95 - 130 | °C | — |
Back Pressure ⁷ | 0.3 - 0.7 | MPa | — |
Screw Speed ⁷ | 40 - 90 | rpm | — |
Shot to Cylinder Size ⁷ | 40 - 60 | % | — |
Vent Depth ⁷ | 0.025 - 0.08 | mm | — |