SABIC's Specialties Business LNP THERMOCOMP EF006 compound is based on Polyetherimide (PEI) resin containing 30% glass fiber. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Polymer Name: Polyether Imide (PEI)

Processing Methods: Injection Molding

Fillers Included: Glass Fiber

Technical Data Sheet

Popular SABIC's Specialties Business Products

View All SABIC's Specialties Business Products

Knowde Enhanced TDS

Identification & Functionality

Chemical Family

Polyetherimide (PEI),

Polyimides (PI)

Fillers Included

Glass Fiber

Polymer Name

Polyether Imide (PEI)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Cost Effective,

High Modulus,

High Stiffness,

High Temperature Resistance,

No Added PFAS,

UL Listed,

Very Good Heat Resistance

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Automotive & Transportation — Transportation

Aerospace & Aviation

Plastics & Elastomers End Uses

Aerospace Applications,

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Garden Equipment,

Home Appliances,

Lawn Equipment,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 V0

Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Stress (Break) ¹¹188MPaASTM D638
Tensile Stress (Break) ¹¹177MPaISO 527
Tensile Stress (Yield, 5 mm/min) ¹¹169MPaISO 527
Tensile Strain (Break, 5 mm/min) ¹¹2%ISO 527
Tensile Strain (Break) ¹¹2.4%ASTM D638
Tensile Strain (Break) ¹¹2.2%ISO 527
Tensile Modulus (at 1 mm/min) ¹¹10350MPaISO 527
Tensile Modulus (at 50 mm/min) ¹¹11440MPaASTM D638
Flexural Stress (Yield, at 2 mm/min) ¹¹235MPaISO 178
Flexural Stress ¹¹263MPaISO 178
Flexural Stress ¹¹270MPaASTM D790
Flexural Modulus (at 2 mm/min) ¹¹9200MPaISO 178
Flexural Modulus ¹¹11370MPaASTM D790
Flexural Modulus ¹¹11510MPaISO 178
Physical Properties
ValueUnitsTest Method / Conditions
Mold Shrinkage (flow) ᵍ ¹¹0.2 - 0.4%SABIC method
Density ¹¹1.52g/cm³ISO 1183
Density ¹¹1.528g/cm³ASTM D792
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹0.15%ASTM D570
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹0.2%ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹0.23%ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹0.5%ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹0.49%ISO 294
Wear Factor Washer ¹¹13010^-10 in^5-min/ft-lb-hrASTM D3702 Modified: Manual
Dynamic COF ¹¹0.55—ASTM D3702 Modified: Manual
Static COF ¹¹0.5—ASTM D3702 Modified: Manual
Moisture Absorption (at 23°C, 50% RH) ¹¹0.21%ISO 62
Thermal Properties
ValueUnitsTest Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹0.0000181/°CISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹0.0000431/°CISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹214°CISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹209°CISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹105°CUL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹105°CUL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹105°CUL 746B
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹203°CASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹0.00003061/°CASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹0.00003091/°CISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹0.00004141/°CASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹0.00004161/°CISO 11359-2
Impact Properties
ValueUnitsTest Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹45kJ/m²ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹10kJ/m²ISO 180/1A
Izod Impact (Unnotched, at 23°C) ¹¹758J/mASTM D4812
Izod Impact (Notched, at 23°C) ¹¹106J/mASTM D256
Instrumented Dart Impact Energy (Peak, at 23°C) ¹¹12JASTM D3763
Multi-Axial Impact ¹¹2JISO 6603
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ⁷150°C—
Drying Time ⁷4 - 6Hrs—
Maximum Moisture Content ⁷0.02%—
Melt Temperature ⁷360 - 400°C—
Rear - Zone 1 Temperature ⁷360 - 380°C—
Middle - Zone 2 Temperature ⁷370 - 390°C—
Front - Zone 3 Temperature ⁷380 - 400°C—
Nozzle Temperature ⁷390 - 400°C—
Mold Temperature ⁷140 - 180°C—
Back Pressure ⁷0.3 - 0.7MPa—
Screw Speed (Circumferential speed) ⁷0.2 - 0.3m/s—
Vent Depth ⁷0.025 - 0.076mm—
Flame Characteristics
ValueUnitsTest Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ᵖmin. 0.75mmUL 94
Note
  • ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
  • ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
  • ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
  • ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

Mexico,

USA

Regional Availability
  • Americas
  • Europe
  • North America