LNP™ THERMOCOMP™ Compound KZ006AXP

Identification & Functionality

Fillers Included

Glass Fiber,

Milled Glass Fiber

Polymer Name

Polyacetal Homopolymer (POM)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyacetals

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Cost Effective,

High Stiffness,

Low Warpage,

No Added PFAS

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Plastics & Elastomers End Uses

Building Materials,

Cell Phones,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Garden Equipment,

Lawn Equipment,

Personal Accessories,

Pool Covers,

Tablets,

Tarpaulins,

Turf Applications,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹	72	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	4150	MPa	ASTM D790
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	45	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	4	%	ASTM D638

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.64	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.8 - 1	%	ASTM D955
Water Absorption (at 23°C, 24hrs) ¹¹	0.3	%	ASTM D570

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	120	°C	ASTM D648

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	180	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	38	J/m	ASTM D256

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	90	°C	—
Drying Time ⁷	4	Hrs	—
Melt Temperature ⁷	200 - 215	°C	—
Mold Temperature ⁷	85 - 110	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 