LNP™ THERMOCOMP™ Compound LC006EX1

Identification & Functionality

Chemical Family

Polyether Ether Ketone (PEEK)

Fillers Included

Carbon Fiber

Polymer Name

Polyetheretherketone (PEEK)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Features & Benefits

Materials Features

Cost Effective,

Easy To Mold,

Electrically Conductive,

Good Moldability,

Good Processability,

High Impact Resistance,

High Modulus,

High Stiffness,

High Strength,

High Temperature Resistance,

Light Weight,

Very Good Heat Resistance

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics,

Industrial

Applications

Consumer Goods — Appliances & Electronics

Industrial — Chemical & Industrial Manufacturing

Equipment & Parts

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays,

Industrial Automation

Electrical & Electronics — Parts & Components

Connectors,

Housings & Enclosures,

Semiconductor Manufacturing,

Switches & Relays

Automotive & Transportation — Transportation

Aerospace & Aviation

Plastics & Elastomers End Uses

5G Dipole Antenna,

Air Cabin Interior,

Cell Phones,

Computer Components,

Cooling Fan,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Electronic Components,

Enclosure,

Heavy Vehicles,

Industrial Applications,

Oil/Gas Applications,

SMT Connector,

Semiconductor Applications,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	276	MPa	ASTM D638
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	1.7	%	ASTM D638
Tensile Modulus (at 5 mm/min) ¹¹	26500	MPa	ASTM D638
Flexural Strength (at 1.3 mm/min, 50 mm span) ¹¹	398	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	21300	MPa	ASTM D790
Tensile Stress (Break, 5 mm/min) ¹¹	267	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.7	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	29200	MPa	ISO 527
Flexural Strength (at 2 mm/min) ¹¹	412	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	25400	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹	0.052	%	ASTM D570
Specific Gravity ¹¹	1.423	—	ASTM D792
Mold Shrinkage (flow) ᵍ ¹¹	0.28	%	SABIC method
Mold Shrinkage (xflow) ᵍ ¹¹	1.1	%	SABIC method
Moisture Absorption (at 23°C, 50% RH, Equilibrium) ¹¹	0.072	%	ISO 62-4
Density ¹¹	1.42	g/cm³	ASTM D792

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹	338	°C	ASTM D648
Heat Deflection Temperature (at 1.82 MPa, 3.2 mm, Unannealed) ¹¹	329	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 120°C, flow) ¹¹	0.0000093	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 120°C, xflow) ¹¹	0.000034	1/°C	ASTM E831
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	337	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	322	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	860	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	97	J/m	ASTM D256
Multi-Axial Impact ¹¹	8.4	J	ASTM D3763
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	56	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	10	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹	55	kJ/m²	ISO 179/1eU
Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹	8	kJ/m²	ISO 179/1eA

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	150	°C	—
Drying Time ⁷	4 - 6	Hrs	—
Front - Zone 3 Temperature ⁷	380 - 400	°C	—
Middle - Zone 2 Temperature ⁷	380 - 400	°C	—
Rear - Zone 1 Temperature ⁷	370 - 380	°C	—
Mold Temperature ⁷	175 - 190	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed ⁷	60 - 100	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 