LNP™ THERMOCOMP™ Compound MB006SXP

Identification & Functionality

Additives Included

Heat Stabilizer,

Mold Release Agent

Chemical Family

Polyolefins,

Polypropylenes (PP)

Fillers Included

Glass Bead,

Glass Fiber

Polymer Name

Polypropylene (unspecified)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Cost Effective,

Good Mold Release,

Heat Stabilized,

High Stiffness,

Low Warpage,

No Added PFAS

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Building Materials

Pipes & Plumbing

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Building Materials,

Cell Phones,

Computer Components,

Consumer Applications,

Containers,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Faucet System Components,

Fittings,

Gears,

Personal Accessories,

Pump Parts,

Sporting Goods,

Tablets,

Water Management

Plastics & Elastomers Processing Methods

Injection Molding

Resins and Compounds for Water Management Applications

SABIC’S specialty resins and compounds offer the water management industry design flexibility to produce products with longer lives and higher quality. Our materials are excellent candidates to replace metal and can provide weight reduction, corrosion resistance, high strength and stiffness or inherent lubricity depending on the application’s requirements.

• Thermal resistance
• Structural mechanical performance

In addition to mechanical requirements, applications for the water management industry need certification for potable water compliance according to national standards. SABIC has developed a dedicated potable water certified portfolio to help our customers accelerate their application development time to market.

SABIC Offerings Certified for Water Management Applications:

For applications that do not require potable water certification, SABIC’s Specialties portfolio includes a wide range of specialized thermoplastic compounds based on different base resins and fillers.

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, 50 mm/min) ¹¹	25	MPa	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹	7.1	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	1900	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	36	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	1700	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (flow) ᵍ ¹¹	1.2 - 1.6	%	SABIC method
Density ¹¹	1.12	g/cm³	ISO 1183

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000107	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.00012	1/°C	ISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	62	°C	ISO 75/Af

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	20	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	4	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	80	°C	—
Drying Time ⁷	4	Hrs	—
Melt Temperature ⁷	225 - 250	°C	—
Front - Zone 3 Temperature ⁷	240 - 250	°C	—
Middle - Zone 2 Temperature ⁷	215 - 225	°C	—
Rear - Zone 1 Temperature ⁷	195 - 205	°C	—
Mold Temperature ⁷	30 - 50	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	30 - 60	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America