LNP™ THERMOCOMP™ Compound UX06032

Identification & Functionality

Additives Included

Flame Retardant,

Heat Stabilizer

Chemical Family

Polyamides

Fillers Included

Glass Fiber

Polymer Name

Polyphthalamide (PPA)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Labeling Claims

Bromine-free,

Chlorine-free,

No Added PFAS

Materials Features

Cost Effective,

Flame Retardant,

Heat Stabilized,

High Stiffness,

High Temperature Resistance,

No Added PFAS,

Non-brominated,

Non-chlorinated,

Very Good Heat Resistance

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Powertrain & UTH

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Electrical & Electronics — Parts & Components

Connectors,

Semiconductor Manufacturing,

Switches & Relays

Plastics & Elastomers End Uses

Appliances,

Automotive Under The Hood,

Cell Phones,

Commercial Appliance,

Computer Components,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Semiconductor Applications,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 V0

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹	130	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	2.1	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	1.14E+04	MPa	ISO 527
Flexural Stress (Break, 2 mm/min) ¹¹	200	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	9900	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹	0.2 - 0.3	%	SABIC method
Density ¹¹	1.46	g/cm³	ISO 1183
Water Absorption (at 23°C, 24hrs) ¹¹	0.23	%	ISO 62-1

Thermal Properties

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000021	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000054	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	275	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	258	°C	ISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹	140	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	140	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	140	°C	UL 746B

Electrical Properties

	Value	Units	Test Method / Conditions
Volume Resistivity ¹¹	1000000000000000 - 100000000000000000	Ω.cm	ASTM D257
Comparative Tracking Index ʳ ¹¹	600	V	IEC 60112
Comparative Tracking Index (UL, PLC) ¹¹	0	PLC Code	UL 746A
Hot Wire Ignition (PLC 0) ¹¹	min. 0.41	mm	UL 746A
High Ampere Arc Ignition (PLC 0) ¹¹	min. 0.41	mm	UL 746A

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	40	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	5	kJ/m²	ISO 180/1A

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120 - 140	°C	—
Drying Time ⁷	4 - 6	Hrs	—
Melt Temperature ⁷	305 - 315	°C	—
Front - Zone 3 Temperature ⁷	295 - 315	°C	—
Middle - Zone 2 Temperature ⁷	290 - 310	°C	—
Rear - Zone 1 Temperature ⁷	280 - 300	°C	—
Mold Temperature ⁷	130 - 150	°C	—
Back Pressure ⁷	0.2 - 0.3	MPa	—
Screw Speed ⁷	40 - 80	rpm	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94V-0 Flame Class Rating) ¹⁷	min. 0.41	mm	UL 94
Glow Wire Ignitability Temperature (at 0.8 mm) ¹⁷	825	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature (at 1.6 mm) ¹⁷	825	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature (at 3.0 mm) ¹⁷	850	°C	IEC 60695-2-13
Glow Wire Flammability Index (at 3 mm) ¹⁷	960	°C	IEC 60695-2-12
Glow Wire Flammability Index (at 0.8 mm) ¹⁷	960	°C	IEC 60695-2-12
Glow Wire Flammability Index (at 1.6 mm) ¹⁷	960	°C	IEC 60695-2-12

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
• ¹⁷ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card. The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America