LNP THERMOCOMP™ Compound - WC003 - SABIC's Specialty

Identification & Functionality

Chemical Family: Polyesters
Fillers Included: Carbon Fiber
Polymer Name: Polybutylene Terephthalate (PBT)
Plastics & Elastomers Functions: Resin
Technologies: Plastics
Product Families: Plastics — Engineering & Specialty Polymers
Polyesters & Copolyesters

Features & Benefits

Labeling Claims: No Added PFAS
Materials Features: Cost Effective,
Electrically Conductive,
High Stiffness,
High Strength,
Light Weight,
No Added PFAS

Applications & Uses

Markets: Automotive & Transportation,
Building & Construction,
Consumer Goods,
Electrical & Electronics,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Automotive & Transportation — Automotive
Powertrain & UTH
Building & Construction — Decorative Materials & Finishes
Artificial Turf
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Lawn & Garden
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Switches & Relays
Consumer Goods — Sports & Recreation
Plastics & Elastomers End Uses: Appliances,
Automotive Under The Hood,
Building Materials,
Cell Phones,
Commercial Appliance,
Computer Components,
Consumer Applications,
Containers,
Displays,
Electrical Components,
Electrical/Electronic Applications,
Fishing Lines,
Fishing Nets,
Garden Equipment,
Home Appliances,
Lawn Equipment,
Personal Accessories,
Pool Covers,
Sporting Goods,
Tablets,
Tarpaulins,
Turf Applications
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Mechanical Properties
Physical Properties
Thermal Properties
Electrical Properties
Impact Properties
Injection Molding
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹	136	MPa	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	1.9	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	11400	MPa	ISO 527
Flexural Stress (Yield, at 2 mm/min) ¹¹	193	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	9600	MPa	ISO 178

	Value	Units	Test Method / Conditions
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹	0.2 - 0.4	%	SABIC method
Density ¹¹	1.36	g/cm³	ISO 1183

	Value	Units	Test Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000016	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000116	1/°C	ISO 11359-2
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80104, sp=64mm) ¹¹	224	°C	ISO 75/Bf
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80104, sp=64mm) ¹¹	206	°C	ISO 75/Af

	Value	Units	Test Method / Conditions
Surface Resistivity ¹¹	100 - 10000	Ω	ASTM D257

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80104, at 23°C) ¹¹	25	kJ/m²	ISO 180/1U
Izod Impact (Notched, 80104, at 23°C) ¹¹	4	kJ/m²	ISO 180/1A

Packaging & Availability

LNP™ THERMOCOMP™ Compound WC003