LNP™ THERMOCOMP™ Compound Z1C00VI

Identification & Functionality

Additives Included

Heat Stabilizer,

Impact Modifier

Fillers Included

Titanium Dioxide

Polymer Name

PPO/PS Alloy

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Chemical Resistant,

Cost Effective,

Excellent Dielectric Properties,

Heat Stabilized,

High Impact Resistance,

High Temperature Resistance,

Impact Modified,

Low Warpage,

No Added PFAS,

UL Listed,

Unreinforced,

Very Good Heat Resistance

Applications & Uses

Markets

Automotive & Transportation,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Automotive & Transportation — Automotive

Interior

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Plastics & Elastomers End Uses

Automotive Interior Parts,

Cell Phones,

Computer Components,

Consumer Applications,

Containers,

Displays,

Electrical Components,

Electrical/Electronic Applications,

Personal Accessories,

Tablets

Plastics & Elastomers Processing Methods

Injection Molding,

Laser Sintering (SLS)

Properties

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹	70	MPa	ASTM D638
Tensile Stress (Break, Type I, 50 mm/min) ¹¹	52	MPa	ASTM D638
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹	4.5	%	ASTM D638
Tensile Strain (Break, Type I, 50 mm/min) ¹¹	8	%	ASTM D638
Tensile Modulus (at 50 mm/min) ¹¹	2700	MPa	ASTM D638
Flexural Stress (Break, 1.3 mm/min, 50 mm span) ¹¹	110	MPa	ASTM D790
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	2700	MPa	ASTM D790
Tensile Stress (Yield, 50 mm/min) ¹¹	70	MPa	ISO 527
Tensile Stress (Break, 50 mm/min) ¹¹	55	MPa	ISO 527
Tensile Strain (Yield, 50 mm/min) ¹¹	4.5	%	ISO 527
Tensile Strain (Break, 50 mm/min) ¹¹	9	%	ISO 527
Tensile Modulus (at 1 mm/min) ¹¹	2800	MPa	ISO 527
Flexural Stress (Break, 2 mm/min) ¹¹	115	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	2800	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Density ¹¹	1.11	g/cm³	ISO 1183
Mold Shrinkage (flow) ᵍ ¹¹	0.5 - 0.7	%	SABIC method

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	155	°C	ISO 75/Bf

Electrical Properties

	Value	Units	Test Method / Conditions
Dielectric Constant (at 1.1 GHz) ¹¹	2.65	—	SABIC method
Dielectric Constant (at 1.9 GHz) ¹¹	2.65	—	SABIC method
Dielectric Constant (at 10 GHz) ¹¹	2.65	—	SABIC method
Dissipation Factor (at 1.1 GHz) ¹¹	0.0012	—	SABIC method
Dissipation Factor (at 1.9 GHz) ¹¹	0.0014	—	SABIC method
Dissipation Factor (at 10 GHz) ¹¹	0.002	—	SABIC method

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Notched, at 23°C) ¹¹	40	J/m	ASTM D256
Izod Impact (Unnotched, at 23°C) ¹¹	600	J/m	ASTM D4812
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	6	kJ/m²	ISO 180/1A
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	50	kJ/m²	ISO 180/1U

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	120	°C	—
Drying Time ⁷	3 - 5	Hrs	—
Melt Temperature ⁷	270 - 320	°C	—
Nozzle Temperature ⁷	280 - 320	°C	—
Front - Zone 3 Temperature ⁷	280 - 310	°C	—
Middle - Zone 2 Temperature ⁷	270 - 300	°C	—
Rear - Zone 1 Temperature ⁷	260 - 290	°C	—
Mold Temperature ⁷	100 - 140	°C	—
Back Pressure ⁷	10	MPa	—
Screw Speed ⁷	100	rpm	—

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability

• Americas
• Asia
• Europe
• North America