NORYL™ Resin GFN20

Identification & Functionality

Additives Included

Flame Retardant,

Mold Release Agent

Fillers Included

Glass Fiber

Polymer Name

PPO/PS Alloy

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Features & Benefits

Labeling Claims

Bromine-free,

Chlorine-free,

No Added PFAS

Materials Features

Amorphous,

Dimensional Stability,

Flame Retardant,

Good Mold Release,

Good Stiffness,

High Hydrolytic Stability,

High Stiffness,

High Strength,

Low Moisture Absorption,

Low Shrinkage,

Low Specific Gravity,

Low Warpage,

No Added PFAS,

Non-Halogenated,

Non-brominated,

Non-chlorinated

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Building Envelope & Roofing

Glazing & Window Elements

Building & Construction — Building Materials

Interior Fixtures

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Electrical & Electronics — Parts & Components

Connectors

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Connectors,

Construction Applications,

Displays,

Electrical/Electronic Applications,

Front Spoiler,

Garden Equipment,

Lawn Equipment,

Pool Covers,

Side Spoiler,

Tablets,

Tarpaulins,

Turf Applications

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 HB

Mechanical Properties

	Value	Units	Test Method / Conditions
Taber Abrasion (CS-17, 1 kg) ¹¹	60	mg/1000cy	SABIC method
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	100	MPa	ASTM D638
Tensile Stress (Yield, 5 mm/min) ¹¹	90	MPa	ISO 527
Tensile Stress (Yield, 5 mm/min) ¹¹	80	MPa	ISO 527
Tensile Stress (Yield, Type I, 10 mm/min) ¹¹	88	MPa	SABIC - Japan Method
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	3	%	ASTM D638
Tensile Stress (Break, 5 mm/min) ¹¹	80	MPa	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	2.5	%	ISO 527
Tensile Strain (Yield, Type I, 10 mm/min) ¹¹	6 - 8	%	SABIC - Japan Method
Tensile Modulus (at 5 mm/min) ¹¹	6500	MPa	ASTM D638
Tensile Strain (Break, 5 mm/min) ¹¹	2.5	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	3	%	ISO 527
Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹	131	MPa	ASTM D790
Tensile Modulus (at 1 mm/min) ¹¹	6000	MPa	ISO 527
Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹	5570	MPa	ASTM D790
Flexural Stress (Break, 2 mm/min) ¹¹	120	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	5400	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	4500	MPa	ISO 178
Ball Indentation Hardness (H358/30) ¹¹	100	MPa	ISO 2039-1
Flexural Stress (Yield, at 2 mm/min) ¹¹	150	MPa	ISO 178

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹	0.2 - 0.4	%	SABIC method
Specific Gravity ¹¹	1.23	—	ASTM D792
Density ¹¹	1.25	g/cm³	ISO 1183
Water Absorption (at 23°C, 24hrs) ¹¹	0.12	%	ISO 62-1
Water Absorption (at 23°C, 24hrs) ¹¹	0.06	%	ASTM D570
Mold Shrinkage (flow) ᵍ ¹¹	0.2 - 0.4	%	SABIC method
Water Absorption (at 23°C, saturated) ¹¹	0.2	%	ISO 62-1
Melt Flow Rate (at 300°C, 5.0 kgf) ¹¹	11.7	g/10 min	ASTM D1238
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.04	%	ISO 62
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.06	%	ISO 62
Melt Volume Rate (at 280°C, 10.0 kg) ¹¹	15	cm³/10 min	ISO 1133
Melt Volume Rate (at 280°C, 5.0 kg) ¹¹	2	cm³/10 min	ISO 1133

Thermal Properties

	Value	Units	Test Method / Conditions
Thermal Conductivity ¹¹	0.26	W/m-°C	ISO 8302
Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹	0.00003	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹	0.00007	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate A/50) ¹¹	145	°C	ISO 306
Vicat Softening Temperature (Rate B/50) ¹¹	140	°C	ISO 306
Vicat Softening Temperature (Rate B/50) ¹¹	135	°C	ISO 306
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	137	°C	ASTM D648
Vicat Softening Temperature (Rate B/120) ¹¹	140	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	147	°C	ISO 306
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹	138	°C	ASTM D648
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹	130	°C	ISO 75/Be
Coefficient of Thermal Expansion (at -30°C to 30°C) ¹¹	0.000028 - 0.000045	1/°C	TMA
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹	120	°C	ISO 75/Ae
Relative Temperature Index (Electrical) ᵖ ¹¹	90	°C	UL 746B
Relative Temperature Index (Electrical) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	90	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	65	°C	UL 746B
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	135	°C	ISO 75/Af
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	90	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	65	°C	UL 746B

Electrical Properties

	Value	Units	Test Method / Conditions
Comparative Tracking Index (UL, PLC) ¹¹	4	PLC Code	UL 746A
High Ampere Arc Ignition (PLC 4) ¹¹	min. 1.5	mm	UL 746A
Hot Wire Ignition (PLC 1) ¹¹	min. 1.5	mm	UL 746A
Hot Wire Ignition (PLC 2) ¹¹	min. 3	mm	UL 746A
High Voltage Arc Track Rate (PLC) ¹¹	4	PLC Code	UL 746A
Arc Resistance (Tungsten, PLC) ¹¹	6	PLC Code	ASTM D495
Volume Resistivity ¹¹	1.00E+15	Ω.cm	IEC 60093
Surface Resistivity (ROA) ¹¹	min. 1.E+15	Ω	IEC 60093
Dielectric Strength (in oil, at 3.2mm) ¹¹	18	kV/mm	IEC 60243-1
Relative Permittivity (1 MHz) ¹¹	2.9	—	IEC 60250
Dissipation Factor (at 50/60 Hz) ¹¹	0.0008	—	IEC 60250
Dissipation Factor (at at 1 MHz) ¹¹	0.003	—	IEC 60250
Comparative Tracking Index ʳ ¹¹	250	V	IEC 60112
Relative Permittivity (50/60 Hz) ¹¹	2.9	—	IEC 60250

Impact Properties

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	23	kJ/m²	ISO 180/1U
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	30	kJ/m²	ISO 180/1U
Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹	23	kJ/m²	ISO 180/1U
Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹	25	kJ/m²	ISO 179/1eU
Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹	25	kJ/m²	ISO 179/1eU
Izod Impact (Unnotched, at 23°C) ¹¹	550	J/m	ASTM D4812
Izod Impact (Notched, at 23°C) ¹¹	88	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	20	J	ASTM D3763
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	10	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80*10*4, at -30°C) ¹¹	9	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹	8	kJ/m²	ISO 179/1eA

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	100 - 120	°C	—
Drying Temperature ⁷	110 - 120	°C	—
Drying Time ⁷	3 - 4	Hrs	—
Drying Time ⁷	2 - 3	Hrs	—
Drying Time (Cumulative) ⁷	8	Hrs	—
Melt Temperature ⁷	280 - 300	°C	—
Melt Temperature ⁷	300 - 325	°C	—
Maximum Moisture Content ⁷	0.02	%	—
Nozzle Temperature ⁷	260 - 280	°C	—
Nozzle Temperature ⁷	300 - 325	°C	—
Front - Zone 3 Temperature ⁷	280 - 300	°C	—
Front - Zone 3 Temperature ⁷	290 - 325	°C	—
Middle - Zone 2 Temperature ⁷	260 - 280	°C	—
Middle - Zone 2 Temperature ⁷	275 - 320	°C	—
Rear - Zone 1 Temperature ⁷	240 - 260	°C	—
Rear - Zone 1 Temperature ⁷	265 - 315	°C	—
Hopper Temperature ⁷	60 - 80	°C	—
Mold Temperature ⁷	80 - 110	°C	—
Mold Temperature ⁷	80 - 120	°C	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed ⁷	20 - 100	rpm	—
Shot to Cylinder Size ⁷	30 - 70	%	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ʳ	min. 1.5	mm	UL 94
UL Recognized (94HB Flame Class Rating) ʳ	1.5	mm	UL 94
UV-light (Water exposure/immersion) ʳ	F1	—	UL 746C
Glow Wire Flammability Index (passes at 750°C) ʳ	3.2	mm	IEC 60695-2-12
Oxygen Index (LOI) ʳ	26	%	ISO 4589

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

China (Mainland)

Regional Availability

• Asia
• Europe