Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, 50 mm/min) ¹¹ | 73 | MPa | ISO 527 |
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 76 | MPa | ASTM D638 |
Tensile Stress (Yield) ¹¹ | 63 | MPa | SABIC - Japan Method |
Tensile Strain (Break) ¹¹ | 8.5 | % | SABIC - Japan Method |
Tensile Stress (Break, 50 mm/min) ¹¹ | 55 | MPa | ISO 527 |
Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 55 | MPa | ASTM D638 |
Flexural Stress ¹¹ | 99 | MPa | ASTM D790 |
Tensile Strain (Yield, 50 mm/min) ¹¹ | 4.5 | % | ISO 527 |
Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 4.7 | % | ASTM D638 |
Flexural Modulus ¹¹ | 2350 | MPa | ASTM D790 |
Tensile Strain (Break, 50 mm/min) ¹¹ | 8 | % | ISO 527 |
Tensile Strain (Break, 50 mm/min) ¹¹ | 8.00E+00 | % | ISO 527 |
Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 9.7 | % | ASTM D638 |
Tensile Modulus (at 1 mm/min) ¹¹ | 2600 | MPa | ISO 527 |
Tensile Modulus (at 50 mm/min) ¹¹ | 2800 | MPa | ASTM D638 |
Flexural Stress (Yield, at 2 mm/min) ¹¹ | 110 | MPa | ISO 178 |
Flexural Stress (Yield, at 6.4 mm) ¹¹ | 114 | MPa | ASTM D790 |
Flexural Modulus (at 2 mm/min) ¹¹ | 2500 | MPa | ISO 178 |
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 113 | MPa | ASTM D790 |
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2840 | MPa | ASTM D790 |
Flexural Modulus (at 6.4 mm) ¹¹ | 2840 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.1 | — | ASTM D792 |
Density ¹¹ | 1.1 | g/cm³ | ISO 1183 |
Melt Volume Rate (at 260°C, 10 kg) ¹¹ | 13 | cm³/10 min | ISO 1133 |
Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 10 | cm³/10 min | ISO 1133 |
Water Absorption (at 23°C, 24hrs) ¹¹ | 0.07 | % | ASTM D570 |
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate (at 250°C, 10.0 kgf) ¹¹ | 3.9 | g/10 min | ASTM D1238 |
Melt Viscosity (at 280°C, 1500 sec⁻¹) ¹¹ | 278 | Pa-s | ISO 11443 |
Value | Units | Test Method / Conditions | |
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
Ball Pressure Test (at 123°C to 127°C) ¹¹ | 125 | — | IEC 60695-10-2 |
Vicat Softening Temperature (Rate B/120) ¹¹ | 140 | °C | ISO 306 |
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 117 | °C | ISO 75/Af |
Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 136 | °C | ASTM D648 |
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 122 | °C | ASTM D648 |
Coefficient of Thermal Expansion (at -30°C to 30°C) ¹¹ | 0.00007 | 1/°C | TMA |
Ball Pressure Test (approximate maximum) ¹¹ | 125 | °C | IEC 60695-10-2 |
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 118 | °C | ASTM D648 |
Vicat Softening Temperature (Rate A/120) ¹¹ | 150 | °C | ISO 306 |
Relative Temperature Index (Electrical) ᵖ ¹¹ | 110 | °C | UL 746B |
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 105 | °C | UL 746B |
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 110 | °C | UL 746B |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index ʳ ¹¹ | 250 | V | IEC 60112 |
Surface Resistivity ¹¹ | 1.00E+16 | Ω | ASTM D257 |
Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
Relative Permittivity (50/60 Hz) ¹¹ | 2.8 | — | ASTM D150 |
High Ampere Arc Ignition (PLC 0) ¹¹ | min. 0.75 | mm | UL 746A |
Hot Wire Ignition (PLC 0) ¹¹ | min. 0.75 | mm | UL 746A |
High Voltage Arc Track Rate (PLC) ¹¹ | 4 | PLC Code | UL 746A |
Arc Resistance (Tungsten, PLC) ¹¹ | 6 | PLC Code | ASTM D495 |
Value | Units | Test Method / Conditions | |
Charpy Impact (Unnotched, at 23°C) ¹¹ | 10 | kJ/m² | ISO 179/2C |
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
Izod Impact (Notched, at 23°C) ¹¹ | 140 | J/m | ASTM D256 |
Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 6 | kJ/m² | ISO 180/1A |
Izod Impact (Notched, 80*10*4, at 0°C) ¹¹ | 11 | kJ/m² | ISO 180/1A |
Izod Impact (Notched, 80*10*4, at -10°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
Izod Impact (Notched, 80*10*4, at -20°C) ¹¹ | 9 | kJ/m² | ISO 180/1A |
Izod Impact (Notched, 80*10*4, at -40°C) ¹¹ | 8 | kJ/m² | ISO 180/1A |
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 11 | kJ/m² | ISO 179/1eA |
Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 9 | kJ/m² | ISO 179/1eU |
Izod Impact (Notched, at -30°C) ¹¹ | 60 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 52 | J | ASTM D3763 |
Charpy Impact (at -30°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 8 | kJ/m² | ISO 179/1eA |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 105 | °C | — |
Drying Temperature ⁷ | 105 - 110 | °C | — |
Drying Time ⁷ | 3 - 4 | Hrs | — |
Drying Time (Cumulative) ⁷ | 8 | Hrs | — |
Maximum Moisture Content ⁷ | 0.02 | % | — |
Melt Temperature ⁷ | 280 - 300 | °C | — |
Melt Temperature ⁷ | 275 - 305 | °C | — |
Front - Zone 3 Temperature ⁷ | 270 - 290 | °C | — |
Front - Zone 3 Temperature ⁷ | 265 - 305 | °C | — |
Middle - Zone 2 Temperature ⁷ | 280 - 300 | °C | — |
Middle - Zone 2 Temperature ⁷ | 255 - 300 | °C | — |
Nozzle Temperature ⁷ | 275 - 305 | °C | — |
Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C | — |
Rear - Zone 1 Temperature ⁷ | 245 - 295 | °C | — |
Hopper Temperature ⁷ | 60 - 80 | °C | — |
Mold Temperature ⁷ | 80 - 100 | °C | — |
Mold Temperature ⁷ | 70 - 100 | °C | — |
Back Pressure ⁷ | 0.3 - 0.7 | MPa | — |
Screw Speed ⁷ | 20 - 100 | rpm | — |
Shot to Cylinder Size ⁷ | 30 - 70 | % | — |
Vent Depth ⁷ | 0.038 - 0.051 | mm | — |
Value | Units | Test Method / Conditions | |
UL Recognized (94-5VA Flame Class Rating) ʳ | min. 2.5 | mm | UL 94 |
UL Recognized (94-5VB Flame Class Rating) ʳ | min. 2 | mm | UL 94 |
UL Recognized (94V-0 Flame Class Rating) ʳ | min. 0.75 | mm | UL 94 |
UL Recognized (94V-2 Flame Class Rating) ʳ | min. 0.4 | mm | UL 94 |
Glow Wire Flammability Index (at 0.75 mm) ʳ | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index (at 1 mm) ʳ | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index (at 1.5 mm) ʳ | 960 | °C | IEC 60695-2-12 |
Glow Wire Flammability Index (at 3 mm) ʳ | 960 | °C | IEC 60695-2-12 |
Glow Wire Ignitability Temperature (at 0.75 mm) ʳ | 750 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature (at 1.0 mm) ʳ | 775 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature (at 1.5 mm) ʳ | 775 | °C | IEC 60695-2-13 |
Glow Wire Ignitability Temperature (at 3.0 mm) ʳ | 775 | °C | IEC 60695-2-13 |
UV-light (Water exposure/immersion) ʳ | F1 | — | UL 746C |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability