Silane crosslinkable polyethylene for low voltage power cable insulation
Applications & Uses
- Markets
- Applications
- Cure Method
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Appearance
- Pellets
- Mechanical Properties
- Physical Properties
- Electrical Properties
| Value | Units | Test Method / Conditions | |
| Elongation at Break | 450 | % | IEC 60811-501 |
| Elongation at Break (After Thermal Aging: 10 Days at 150°C) | -18 | % Variation | IEC 605811-401 |
| Elongation Under Load (20N/cm² at 200°C) (Cure Assessment by Hot Set Test: Force cured at 80°C in Water) | 80 | % | IEC 60811-507 |
| Permanent Elongation (After Cooling) | 5 | % | IEC 60811-507 |
| Tensile Strength (at Break) | 18 | N/mm² | IEC 60811-501 |
| Tensile Strength at Break (After Thermal Aging: 10 Days at 150°C) | 20 | % Variation | IEC 605811-401 |
| Value | Units | Test Method / Conditions | |
| Density | 0.95 | g/cm³ | BS EN ISO 1183-3 |
| Value | Units | Test Method / Conditions | |
| Permittivity (50Hz at 23°C) | 3.47 | — | IEC 60250 |
| Power Factor (50Hz at 23°C) | 0.0017 | — | IEC 60250 |
| Volume Resistivity (at 20°C) | 1.5 x 10¹⁶ | Ohm.cm | BS EN 50395 |
Technical Details & Test Data
- Processing
Extruder: Most modern thermoplastic extruders will process this compound, particularly if a screw suitable for polyethylene extrusion is available.
Extruder temperature conditions: It is important that the melt temperature is not allowed to increase above 190oC. As a guide the following temperature profile is recommended:Zone #1 Zone #2 Zone #3 Zone #4 Head Die Celsius 150°C 160°C 170°C 180°C 185°C 190°C Fahrenheit 302°F 320°F 338°F 356°F 365°F 374°F This profile will vary slightly depending on extruder type, head design and output. Initial purging of the extruder should be performed without the addition of catalyst masterbatch to reduce risks of precuring.
Screw Water Temperature: Not mandatory, if present we recommend 60-70°C
Recommended Screen Pack: 30, 100, 30 (mesh aperture per linear inch) or 600,150, 600 micronHead & Tool Design - The head and tools should be so designed as to allow streamlined flow without the possibility of stagnation of material (where pre-curing could take place). To obtain the optimum in physical properties in the case of tubing tools, it is generally recommended that a draw down ratio not greater than 2.6 is used.
Crosslinking or Cure: A fast cure can be obtained either by immersion in hot water or exposure to low pressure steam at a temperature up to 70°C; this particular system has ambient cure, usually between 5 and 7 days.
Catalyst & Color Masterbatches - CM493 or CM497 catalyst masterbatch is normally added at 5% to 95% of SX523 black graft. The choice of the correct catalyst will be made based on the equipment and processing conditions, please contact on technical team for recommendation. It is recommended that all catalyst masterbatches should be thoroughly dried at 60°C for 8 hours or at 80°C for 4 hours.
Packaging & Availability
- Packaging
The following possibilities are available:
- Moisture resistant sacks containing 25kg.
- Boxes with a moisture resistant heat sealed liner containing approximately 500kg
Storage & Handling
- Storage & Shelf Life
A period of at least 6 months from date of manufacture can normally be expected. The following storage conditions are recommended:
- Packaging should remain sealed.
- Avoid temperature above 30C.
- Avoid storage outside and in direct sunlight.
- Use within 8 hours of opening packaging.