VINNOL® H 11/59 is a copolymer composed of approximately 89 wt.% vinyl chloride (VC) and 11 wt.% vinyl acetate (VAc). Its primary application lies in serving as a binder for surface coating compounds and printing inks. As a thermoplastic and physically drying binder, VINNOL® H 11/59 undergoes a film-forming process when the solvent within the formulation evaporates.

VINNOL® H 15/45 M Special is a specialized carboxylate-containing terpolymer composed of approximately 84 wt.% vinyl chloride (VC), 15 wt.% vinyl acetate (VAc), and 0.5 wt.% dicarboxylic acid. Its primary application is as a binder for surface coating compounds and printing inks. This thermoplastic and physically drying binder creates a film as the solvent within the formulation evaporates.

VINNOL® E 18/38 is a copolymer consisting of approximately 82 wt.% vinyl chloride (VC) and 18 wt.% vinyl acetate (VAc). It is primarily utilized as a binder in printing inks and surface coating compounds. This thermoplastic binder undergoes a physically drying process, resulting in the formation of a film as the solvent within the formulation evaporates.

GENIOSIL® XL 10 is an alkoxyvinyl silane compound. When exposed to moisture, the silane undergoes hydrolysis, resulting in the release of methanol. This hydrolysis process leads to the formation of silanols, which have the ability to react with each other and form siloxanes. The applications of GENIOSIL® XL 10 include marine and protective coatings, plastic additives, and plastic crosslinking.

WACKER® Silicate TES 28 is a monomeric ethyl silicate, also known as tetraethoxysilane or tetraethyl orthosilicate. It is a colorless, low-viscosity liquid with an SiO2 content of approximately 28 wt.%. This product is commonly used in the formulation of anti-corrosive coatings, marine and protective coatings, as well as industrial coatings.

VINNOL® H 40/50 is a copolymer composed of approximately 63 wt.% vinyl chloride (VC) and approximately 37 wt.% vinyl acetate (VAc). Its primary application is as a binder for surface coating compounds and printing inks. This thermoplastic binder undergoes physical drying, resulting in the formation of a film as the solvent within the formulation evaporates.

VINNOL® H 40/55 is a copolymer comprising approximately 62 wt.% vinyl chloride (VC) and approximately 38 wt.% vinyl acetate (VAc). Its primary application lies in serving as a binder for surface coating compounds and printing inks. Functioning as a thermoplastic, physically drying binder, VINNOL® H 40/55 undergoes film formation once the solvent present in the formulation has evaporated.

VINNOL® E 15/45 is a copolymer composed of approximately 85 wt.% vinyl chloride (VC) and 15 wt.% vinyl acetate (VAc). It serves as a binder for surface coating compounds and printing inks. This thermoplastic binder undergoes a physically drying process, resulting in the formation of a film as the solvent within the formulation evaporates.

SILRES® HK 46 is a high-molecular-weight methyl silicone resin supplied as a 50 wt.% solution in xylene-butanol 4:1. It is commonly used as a binder for high heat-resistant coatings and heat-stable nonstick coatings. SILRES® HK 46 is suitable for various heat-resistant paints and is an excellent choice for (anti-corrosion) coatings on fireplaces, mufflers, exhaust systems, engine parts, boilers, furnaces, ovens and oven inserts, chimneys, barbeques, electric and gas heaters, and incinerators.

WACKER® Silicate S100 is a ready-to-use ethyl silicate binder with a flash point above 21°C. It is primarily used for formulating single-pack ethyl silicate zinc-rich primers, which are commonly used as anti-corrosive coatings. This product is particularly suitable for applications in marine, protective, and industrial coatings.

VINNOL® H 40/60 is a copolymer composed of approximately 61 wt.% vinyl chloride (VC) and approximately 39 wt.% vinyl acetate (VAc). Primarily, it serves as a binder for surface coating compounds and printing inks. As a thermoplastic binder, VINNOL® H 40/60 undergoes physical drying, resulting in the formation of a film as the solvent in the formulation evaporates.

WACKER® Silicate MKS is an ethyl silicate binder suitable for the formulation of one-pack ethyl silicate zinc-rich primers. These primers are excellent anti-corrosive coatings. WACKER® Silicate MKS is a binder with outstanding anti-setting properties. Paints formulated with it are easy to stir up, even if they have been stored for a long time.

GENIOSIL® GF 80 is an epoxy functional alkoxysilane. When used as a coupling agent in mineral-filled plastics, it enhances filler dispersibility, reduces sedimentation tendency, and significantly lowers the resin's viscosity. Moreover, it allows for higher filler loading and provides notable improvements in water (vapor) resistance, as well as resistance to acids and bases. In the realm of adhesives and sealants, incorporating GENIOSIL® GF 80 enhances adhesion to the substrate and improves mechanical properties like flexural strength, tensile strength, and modulus of elasticity.

HDK® H17 is a synthetic, hydrophobic, amorphous silica produced via flame hydrolysis. It is a white colloidal powder of high purity. HDK® H17 is used as a thickening and thixotropic agent in composites, coatings, adhesives, and sealants, particularly in vinylester, epoxy, and polyurethane systems.

VINNOL® E 15/45 M is a carboxylate-containing terpolymer consisting of approximately 84 wt.% vinyl chloride (VC), 15 wt.% vinyl acetate (VAc), and 1 wt.% dicarboxylic acid. It functions primarily as a binder in surface coating compounds and printing inks. This thermoplastic binder undergoes a physically drying process, resulting in the formation of a film as the solvent within the formulation evaporates.

WACKER® Silicate TES 40 WN is an ethyl silicate polymer. It is a low-viscosity liquid that provides approximately 41% of silicon dioxide (silica) upon complete hydrolysis. WACKER® Silicate TES 40 WN is used for the precipitation of polymeric SiO2 structures (silica) upon complete hydrolysis, with ethanol being produced as a by-product.

SILRES® IC 232 is a solventless, reactive, methoxyfunctional methyl-phenyl polysiloxane with a narrow molecular weight distribution. It is highly suitable for blending with other binder systems to introduce a compatible silicone component. This addition helps to enhance the weathering or heat resistance of the resulting mixture or formulation.

VINNOL® H 15/45 M is a carboxylate-containing terpolymer consisting of approximately 84 wt.% vinyl chloride (VC), 15 wt.% vinyl acetate (VAc), and 1 wt.% dicarboxylic acid. It is primarily employed as a binder in surface coating compounds and printing inks. VINNOL® H 15/45 M functions as a thermoplastic, physically drying binder that undergoes film formation as the solvent within the formulation evaporates.

HDK® N20 is a synthetic, hydrophilic, amorphous silica produced through flame hydrolysis. It is a standard product widely used in various industrial applications. This white colloidal powder offers high purity and serves multiple purposes. One of the primary applications of HDK® N20 is as a thickening and thixotropic agent in organic systems such as unsaturated polyesters, coatings, printing inks, adhesives, and cosmetics. Additionally, it functions as a reinforcing filler in elastomers, particularly silicone elastomers.

VINNOL® H 30/48 M is a terpolymer consisting of approximately 70 wt.% vinyl chloride (VC), 29 wt.% vinyl acetate (VAc), and 1 wt.% dicarboxylic acid. It contains carboxylate groups within its structure. This product is primarily employed as a binder for surface coating compounds and printing inks. VINNOL® H 30/48 M acts as a thermoplastic, physically drying binder that forms a film upon evaporation of the solvent in the formulation.

HDK® H13L is a synthetic, hydrophobic, amorphous silica produced via flame hydrolysis. It is a white colloidal powder of high purity. HDK® H13L is primarily used as a thickening, thixotropic, and anti-sedimentation agent in various applications such as coatings, printing inks, adhesives, and others. It finds its main application in polar systems. The strong hydrophobicity of HDK® H13L makes it particularly suitable for solvent-free systems, high solids formulations, and waterborne coatings.

VINNOL® H 40/43 is a copolymer composed of approximately 66 wt.% vinyl chloride (VC) and approximately 34 wt.% vinyl acetate (VAc). Its primary application is as a binder for surface coating compounds and printing inks. This thermoplastic binder undergoes physical drying, resulting in the formation of a film once the solvent in the formulation has evaporated.

VINNOL® H 15/42 is a copolymer consisting of approximately 86 wt.% vinyl chloride (VC) and 14 wt.% vinyl acetate (VAc). Its primary application is as a binder in surface coating compounds and printing inks. This thermoplastic and physically drying binder undergoes film formation as the solvent present in the formulation evaporates.

HDK® H18 is a synthetic, hydrophobic, amorphous silica produced via flame hydrolysis. It is a white colloidal powder of high purity. HDK® H18 is used as a thickening and thixotropic agent in composites, coatings, adhesives, and sealants, particularly in vinylester, epoxy, and polyurethane systems.

VINNOL® E 15/48 A is a hydroxyl-containing copolymer composed of approximately 84 wt.% vinyl chloride (VC) and 16 wt.% acrylic acid esters. It serves as a binder in surface coating compounds and printing inks. This thermoplastic binder undergoes a physically drying process, resulting in the formation of a film as the solvent within the formulation evaporates.

SILRES® WH 101 A is a water-reducible, solvent-free emulsion of a functional silicone resin. It can be applied as-is or as a formulated product to serve as a water-repellent treatment. SILRES WH 101 A improves substrate longevity when applied over wood or many other materials.

VINNOL® E 15/40 A is a hydroxyl-containing copolymer comprising approximately 84 wt.% vinyl chloride (VC) and 16 wt.% acrylic acid esters. Its primary application lies in serving as a binder for surface coating compounds and printing inks. This thermoplastic binder undergoes a physically drying process, resulting in the formation of a film as the solvent within the formulation evaporates.

SILRES® HP 2020 is a low-viscosity, reactive aminofunctional methyl phenyl silicone resin. The product is typically used as a curing agent or crosslinker for cycloaliphatic epoxy resins in 2-pack high-solids coatings. It significantly improves the weathering resistance of the coating compared to organic amine curing agents. Such 2-pack epoxypolysiloxane coatings are an isocyanate-free alternative to 2-pack polyurethanes as weathering-resistant topcoats.

SILESTER® XAR is a ready-to-use, prehydrolyzed ethyl silicate hybrid binder. The solvent used in SILESTER® XAR is a blend of ethanol and 2-propanol. This product is conveniently prepared and can be directly utilized in the production of ceramic slips, ramming mixes, and anticorrosion paints without any further processing steps.

VINNOL® E 22/48 A is a copolymer composed of approximately 75 wt.% vinyl chloride (VC) and 25 wt.% carbon acid esters with hydroxyl functionality. It serves as a binder for surface coating compounds and printing inks. As a thermoplastic and physically drying binder, VINNOL® E 22/48 A undergoes film formation as the solvent within the formulation evaporates.

SILRES® HP 2000 is a reactive aminofunctional methyl phenyl silicone resin supplied as an approximately 90 wt.% solution in xylene. The product is typically used as a curing agent or crosslinker for cycloaliphatic epoxy resins in 2-pack high-solids coatings. It significantly improves the weathering resistance of the coating compared to organic amine curing agents. Such 2-pack epoxypolysiloxane coatings are an isocyanate-free alternative to 2K-polyurethanes as weathering-resistant topcoats.

SILRES® IC 368 is a solventless, reactive, methoxyfunctional methyl-phenyl polysiloxane with a narrow molecular weight distribution. It is specifically designed to enhance the weathering and heat resistance of organic resins. This solvent-free liquid resin is ideal for incorporating a compatible silicone component into other binder systems. Its properties make it a valuable additive for improving the overall performance and durability of the resulting materials.