Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Basis
- Universal gerneral purpose resin
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Properties
unfilled
slow curing
Applications & Uses
- Applications
- Cure Method
- Plastics & Elastomers End Uses
- Applications
Laminating resin for fabrics
Bonding resin for fillers
for large volume back fillings- Processing Instructions
The temperature of material and processing should be between 18 and 25° C.
The mixing of resin and hardener should be made intensively and if possible without any bubbles at room temperature. We recommend a post curing with a temperature rise of about 10°C/hour.
Difficult geometries should be supported during the curing cycle. Afterwards the part should be cooled down at about 20°C/hour.
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Shore hardness | 87 ± 3 | Shore D | DIN ISO 7619-1 |
| Compressive Strength | 100 ± 8 | MPa | EN ISO 604 |
| Viscosity (25°C) | 550 ± 100 | mPa.s | — |
| Flexural elongation at break | 4.7 ± 0.5 | % | EN ISO 178 |
| Density (20°C) | 1,12 ± 0,02 | g/cm3 | — |
| Flexural modulus | 3000 ± 200 | MPa | EN ISO 178 |
| Pot Life (200g/20°C) | 65 - 75 | minutes | — |
| Flexural strength | 105 ± 5 | MPa | EN ISO 178 |
| Curing time at RT | 18 - 20 | Hrs | — |
| Heat resistance (HDT) | 76 ± 2 | °C | DIN EN ISO 75 B |
| Impact resistance (Charpy) | 37 ± 10 | kJ/m2 | EN ISO 179 |
Packaging & Availability
- Packages
5,000 kg / 10,000 kg / 25,000 kg / 50,000 kg / 220,000 kg 1 kg / 2,5 kg / 5 kg / 25 kg / 50 kg
Storage & Handling
- Storing
At appropriate storage 18-25°C.
Occuring crystallization due to disadvantageous storage conditions can be made return by warming up the material at approx. 60° C for some hours. Opened containers should be closed immediately after use and be protected against moisture. This material should be used up as soon as possible.
Shelf life is indicated on the labels