Flexible casting resin
Features & Benefits
- Materials Features
- Properties
shore A hardness 83
shore hardness (flexibility) variable till A 30
excellent flow properties
transparent
easily dyeable
odorless
high tear strength
free of mercury
RoHS conform
seawater steady - according to DIN 50905
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Applications
Prototypes with rubber-like properties
Flexible parts
jet mask- Processing Instructions
Material- and processing temperature between 18°C and 25°C.
Mixing ratio resin and hardener according instructions.
When using pigment paste, it needs to stir it in Comp.B.
To reach shore hardness A 65 mix GM 956 Comp. A, GM 956-30 Comp. B and GM 956-80 Comp. B as follows:
GM 956 Comp. A (100 weight contents) + GM 956-30 Comp. B (100 weight contents) + GM 956-80 Comp. B (40 weight contents)
First step is the mixture of the B-components, second step: stir B components in Comp. A.
Mold temperature for fabircation of vacuum casting parts: 70°C
Final properties reached after 7 days at room temperature or 4 hrs. post curing at 70°C
Any resin residues at mixing rods, can be removed with ebalta cleaning Agent.
To accelerate use our Accelerator 08.
Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
Tensile strength | 8 ± 1 | MPa | ISO 37 |
Viscosity (25°C) | 2000 ± 200 | mPa.s | — |
Elongation at break / test piece type 2 | 600 ± 75 | % | ISO 37 |
Density (20°C) | 1,04 ± 0,02 | g/cm3 | — |
Shore hardness | 83 ± 3 | Shore D | DIN ISO 7619-1 |
Pot Life (200g/20°C) | 15 - 20 | minutes | — |
Tear resistance arch shaped test piece with incision 1 mm | 15 ± 1 | kN/m | DIN ISO 34-1 |
Curing Time (70°C) | 2 | Hrs | — |
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
Packaging & Availability
- Sales Units (Packages)
Units
- Comp. A GM 956 Comp. A (Isocyanate) 1,000 kg / 5,000 kg
- Comp. B GM 956-80 Comp. B (polyol)e) 0,800 kg / 4,000 kg
Storage & Handling
- Storing
- Storage at room temperature 18-25 °C.
- Opened containers should be closed immediately after use and should be used up as soon as possible.
- Shelf life is indicated on the labels.