Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Basis
- PU casting resin
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Properties
very abrasion resistant
hard flexible
no brittleness phase
very well castable
long potlife
Shore D hardness approx. 65
Applications & Uses
- Markets
- Plastics & Elastomers Processing Methods
- Applications
Core boxes
fixtures- Processing Instructions
- Material- and processing temperature: between 18 - 25 °C.
- Close containers after use.
- Seal porous mold surfaces first (ebalta mold sealer).
- For optimum mold releasing we recommend a special release agent (like T1-1), which can be applied easily with a brush or be sprayed. Releasing of the mold 2-3 times, evaporate for about 20 min. after each releasing.
- Mixing ratio resin/hardener according to instructions.
- Stirring rods etc. with residual resin can be easily cleaned with ebalta cleaning agent.
Important processing instructions:
- B comp. (amine) must be stirred in and carefully mixed into A comp. (isocyanate). The material must be free of streaks.
Properties
- Typical Properties
Value | Units | Test Method / Conditions | |
Wear jet test | ca 41 | W(V/t) [mm³/min] | — |
Viscosity (25°C) | 3500 ± 500 | mPa.s | — |
Elongation of tensile strength | 311 ± 8 | % | — |
Density (20°C) | 1,15 ± 0,02 | g/cm3 | — |
Flexural enlongation at flexural strength | 7 ± 0.5 | % | EN ISO 178 |
Pot Life (200g/20°C) | 30 - 45 | minutes | — |
Flexural modulus | 787 ± 40 | MPa | EN ISO 178 |
Curing time at RT | 12-15 | Hrs | — |
Flexural strength | 28 ± 1 | MPa | EN ISO 178 |
Shore hardness | 65 ± 2 | Shore A | DIN ISO 7619-1 |
Tensile strength | 39 ± 2 | kN/m | — |
Packaging & Availability
- Packages
Packing size B-Pack GM 984-1 / Comp. A+B 8 x 0,300 kg Comp. A/8 x 0,390 kg Comp. B = 5,520 kg
Storage & Handling
- Storing
Storage at room temperature 18-25 °C.
Opened containers should be closed immediately after use and should be used up as soon as possible.