Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Labeling Claims
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Rheological Calculation Properties
- Other Properties
- Mechanical Properties (TPE)
- Rheological Properties
| Value | Units | Test Method / Conditions | |
| Charpy Notched Impact Strength (at +23°C) | N | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength (at -30°C) | N | kJ/m² | ISO 179/1eA |
| Izod Notched Impact Strength (at +23°C) | N | kJ/m² | ISO 180/1A |
| Izod Notched Impact Strength (at -20°C) | N | kJ/m² | ISO 180/1A |
| Tensile Notched Impact Strength (at +23°C) | N | kJ/m² | ISO 8256/1 |
| Value | Units | Test Method / Conditions | |
| Melting Temperature (10°C/min) | 180 | °C | ISO 11357-1/-3 |
| Glass Transition Temperature (at 10°C/min) | -80 | °C | ISO 11357-1/-2 |
| Glass Transition Temperature from DMTA (tan d) | -74 | °C | ASTM D5026/D7028 |
| Coefficient of Linear Thermal Expansion (parallel) | 2.2 | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 2.2 | E-4/°C | ISO 11359-1/-2 |
| Burning Behaviour (at 1.5 mm Nominal Thickness) | UL HB | class | IEC 60695-11-10 |
| Relative Temperature Index (Electrical, 1.5 mm) | 50 | °C | UL746B |
| Relative Temperature Index (with impact, 1.5 mm) | 50 | °C | UL746B |
| Relative Temperature Index (without impact, 1.5 mm) | 50 | °C | UL746B |
| Value | Units | Test Method / Conditions | |
| Volume Resistivity | 5E12 | Ohm*m | IEC 62631-3-1 |
| Value | Units | Test Method / Conditions | |
| Density of Melt | 905 | kg/m³ | — |
| Value | Units | Test Method / Conditions | |
| Water Absorption | 0.8 | % | Sim. to ISO 62 |
| Density | 1080 | kg/m³ | ISO 1183 |
| Apparent Density | 645 | kg/m³ | ISO 60 |
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 25 | MPa | ISO 527-1/-2 |
| Stress at 5% strain | 1.2 | MPa | ISO 527-1/-2 |
| Stress at 10% strain | 2.1 | MPa | ISO 527-1/-2 |
| Stress at 50% strain | 4.4 | MPa | ISO 527-1/-2 |
| Stress at 100% strain | 5.1 | MPa | ISO 527-1/-2 |
| Stress at Break | 16 | MPa | ISO 527-1/-2 |
| Strain at Break | >300 | % | ISO 527-1/-2 |
| Nominal Strain at Break | 900 | % | ISO 527-1/-2 |
| Shore A Hardness (3s) | 85 | — | ISO 868 |
| Shore D Hardness (3s) | 25 | — | ISO 868 |
| Value | Units | Test Method / Conditions | |
| Melt Volume-Flow Rate (at 230 / * °C, 2.16 / * kg) | 45 | cm³/10min | ISO 1133 |
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
Technical Details & Test Data
- Chemical Resistance
Chemical Type Chemical Name Resistance Other Acetic acid (10% by mass) at 23°C resistant Ketones Acetone at 23°C resistant Other Ammonium hydroxide (10% by mass) at 23°C limited resistant, tests necessary to verify Other ASTM 1 at 23°C resistant Other ASTM 3 at 23°C resistant Other Brake fluids (DOT 3/4) at 23°C not resistant Other Calcium chloride (10% by mass) at 23°C limited resistant, tests necessary to verify Other Chloroform at 23°C not resistant Ethers Diethyl ether at 23°C limited resistant, tests necessary to verify Alcohols Ethanol at 23°C limited resistant, tests necessary to verify Other Ethyl Acetate at 23°C limited resistant, tests necessary to verify Other Fuel; Diesel at 85°C resistant Other Hydrochloric acid (10% by mass) at 23°C resistant Other Hydrogen peroxide (30% by mass) at 23°C limited resistant, tests necessary to verify Other Nitric acid (10% by mass) at 23°C resistant Other Phosphoric acid (10% by mass) at 23°C resistant Other Sodium hydroxide (10% by mass) at 23°C resistant Other Sulfuric acid (30% by mass) at 23°C resistant Other Tetrachloroethylene at 23°C limited resistant, tests necessary to verify Hydrocarbons Toluene at 23°C resistant Other Transformer oil at 23°C not resistant Other Trichloroethylene at 23°C not resistant Other Water at 23°C resistant Other Zinc chloride (10% by mass) at 23°C resistant - Creep Modulus-Time 23°C
- Creep Modulus-Time 60°C
- Dynamic Shear Modulus (G)-Temperature
- Dynamic Tensile Modulus (E)-Temperature
- Specific Volume-Temperature (pvT)
- Viscosity-Shear Rate