Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Brake Tubing With Arnitel® CM622 Application Data
Benefits
- Arnitel® TPC allows for light weight solutions (75% lighter compared to rubber)
- Arnitel® TPC allows for cost effective solutions (up to 50% lower system costs than rubber)
- Arnitel® TPC allows for sustainable solutions (compared to PA12, Arnitel® is a plasticizer free solution)
- Arnitel® TPC allows for reliable solutions due to its peak temperatures resistance up to 180°C – 200°C and its good heat aging due to continuous use temperatures 120°C – 170°C
- Hydraulic Hoses Application Data
Details
Arnitel® is used as liner material in multilayer reinforced hydraulic hoses that are in direct contact with various hydraulic fluids.
Benefits
- Arnitel® allows easy extrusion
- Arnitel® has good resistance against hydraulic fluids
- Arnitel® offers good low temperature flexibility
- Arnitel® allows for high peak temperature resistance
Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Other Properties
- Mechanical Properties (Die Cutting)
- Mechanical Properties (TPE)
- Rheological Properties
| Value | Units | Test Method / Conditions | |
| Yield Stress | 20 | MPa | ISO 527-1/-2 |
| Yield Strain | 29 | % | ISO 527-1/-2 |
| Flexural Modulus | 305 | MPa | ISO 178 |
| Charpy Impact Strength (at +23°C) | N | kJ/m² | ISO 179/1eU |
| Charpy Impact Strength (at -30°C) | N | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength (at +23°C) | N | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength (at -30°C) | 12 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact Strength (at +23°C) | N | kJ/m² | ISO 180/1A |
| Value | Units | Test Method / Conditions | |
| Melting Temperature (10°C/min) | 212 | °C | ISO 11357-1/-3 |
| Vicat Softening Temperature (50°C/h 10N) | 200 | °C | ISO 306 |
| Vicat Softening Temperature (50°C/h 50N) | 125 | °C | ISO 306 |
| Coefficient of Linear Thermal Expansion (parallel) | 1.5 | E-4/°C | ISO 11359-1/-2 |
| Coefficient of Linear Thermal Expansion (normal) | 1.5 | E-4/°C | ISO 11359-1/-2 |
| Value | Units | Test Method / Conditions | |
| Relative Permittivity (1 MHz) | 4.1 | — | IEC 62631-2-1 |
| Dissipation Factor (1 MHz) | 170 | E-4 | IEC 62631-2-1 |
| Volume Resistivity | 1.2E11 | Ohm*m | IEC 62631-3-1 |
| Electric Strength | 22 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Value | Units | Test Method / Conditions | |
| Water Absorption | 0.63 | % | Sim. to ISO 62 |
| Humidity Absorption | 0.18 | % | Sim. to ISO 62 |
| Density | 1240 | kg/m³ | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Stress at Break (normal) | 52 | MPa | ISO 527-1/-2 |
| Strain at Break (normal) | 750 | % | ISO 527-1/-2 |
| Tear Strength (normal) | 156 | kN/m | ISO 34-1; Method B |
| Tear Strength (parallel) | 168 | kN/m | ISO 34-1; Method B |
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 310 | MPa | ISO 527-1/-2 |
| Stress at 5% strain | 11 | MPa | ISO 527-1/-2 |
| Stress at 10% strain | 16 | MPa | ISO 527-1/-2 |
| Stress at 50% strain | 19 | MPa | ISO 527-1/-2 |
| Stress at 100% strain | 16 | MPa | ISO 527-1/-2 |
| Stress at 300% strain | 20 | MPa | ISO 527-1/-2 |
| Stress at Break | 35 | MPa | ISO 527-1/-2 |
| Strain at Break | >300 | % | ISO 527-1/-2 |
| Shore D Hardness (3s) | 59 | — | ISO 868 |
| Value | Units | Test Method / Conditions | |
| Melt Volume-Flow Rate (at 230 / * °C, 2.16 / * kg) | 3.7 | cm³/10min | ISO 1133 |
Regulatory & Compliance
- Certifications & Compliance
- Quality Standards
Technical Details & Test Data
- Chemical Resistance
Chemical Type Chemical Name Resistance Other Acetic acid (10% by mass) at 23°C resistant Ketones Acetone at 23°C resistant Other Ammonium hydroxide (10% by mass) at 23°C limited resistant, tests necessary to verify Other ASTM 1 at 23°C resistant Other ASTM 3 at 23°C resistant Other Brake fluids (DOT 3/4) at 23°C not resistant Other Calcium chloride (10% by mass) at 23°C limited resistant, tests necessary to verify Other Chloroform at 23°C not resistant Ethers Diethyl ether at 23°C limited resistant, tests necessary to verify Alcohols Ethanol at 23°C limited resistant, tests necessary to verify Other Ethyl Acetate at 23°C limited resistant, tests necessary to verify Other Fuel; Diesel at 85°C resistant Other Hydrochloric acid (10% by mass) at 23°C resistant Other Hydrogen peroxide (30% by mass) at 23°C limited resistant, tests necessary to verify Other Nitric acid (10% by mass) at 23°C resistant Other Phosphoric acid (10% by mass) at 23°C resistant Other Sodium hydroxide (10% by mass) at 23°C resistant Other Sulfuric acid (30% by mass) at 23°C resistant Other Tetrachloroethylene at 23°C limited resistant, tests necessary to verify Hydrocarbons Toluene at 23°C resistant Other Transformer oil at 23°C not resistant Other Trichloroethylene at 23°C not resistant Other Water at 23°C resistant Other Zinc chloride (10% by mass) at 23°C resistant - Dynamic Tensile Modulus (E)-Temperature
- Shearstress-Shear Rate
- Stress-Strain (TPE)
- Viscosity-Shear Rate
Packaging & Availability
- Packaging Type