- Brake Tubing With Arnitel® CM622 Application Data
Benefits
- Arnitel® TPC allows for light weight solutions (75% lighter compared to rubber)
- Arnitel® TPC allows for cost effective solutions (up to 50% lower system costs than rubber)
- Arnitel® TPC allows for sustainable solutions (compared to PA12, Arnitel® is a plasticizer free solution)
- Arnitel® TPC allows for reliable solutions due to its peak temperatures resistance up to 180°C – 200°C and its good heat aging due to continuous use temperatures 120°C – 170°C
Properties
- Mechanical Properties
- Thermal Properties
- Other Properties
- Mechanical Properties (TPE)
- Rheological Properties
| Value | Units | Test Method / Conditions | |
| Nominal Strain at Break | >50 | % | ISO 527-1/-2 |
| Charpy Notched Impact Strength (at +23°C) | 21 | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength (at -30°C) | 11 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact Strength (at +23°C) | 21 | kJ/m² | ISO 180/1A |
| Izod Notched Impact Strength (at -30°C) | 10 | kJ/m² | ISO 180/1A |
| Value | Units | Test Method / Conditions | |
| Melting Temperature (10°C/min) | 212 | °C | ISO 11357-1/-3 |
| Glass Transition Temperature from DMTA (E) | -30 | °C | ASTM D5026/D7028 |
| Vicat Softening Temperature (50°C/h 10N) | 200 | °C | ISO 306 |
| Vicat Softening Temperature (50°C/h 50N) | 110 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Water Absorption in Water (at 23°C after 24h) | 0.48 | % | ISO 62 |
| Humidity Absorption | 0.16 | % | Sim. to ISO 62 |
| Density | 1230 | kg/m³ | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 260 | MPa | ISO 527-1/-2 |
| Stress at 5% strain | 11.4 | MPa | ISO 527-1/-2 |
| Stress at 10% strain | 16.5 | MPa | ISO 527-1/-2 |
| Stress at 50% strain | 20.9 | MPa | ISO 527-1/-2 |
| Stress at 100% strain | 22.1 | MPa | ISO 527-1/-2 |
| Stress at Break | 31 | MPa | ISO 527-1/-2 |
| Nominal Strain at Break | 250 | % | ISO 527-1/-2 |
| Compression Set Under Constant Strain (at 70°C) | 29 | % | ISO 815 |
| Tear Strength | 148 | kN/m | ISO 34-1; Method B |
| Shore A Hardness (3s) | 98 | — | ISO 868 |
| Shore A Hardness (15s) | 98 | — | ISO 868 |
| Shore D Hardness (3s) | 57 | — | ISO 868 |
| Shore D Hardness (15s) | 57 | — | ISO 868 |
| Value | Units | Test Method / Conditions | |
| Melt Volume-Flow Rate (at 230 / * °C, 2.16 / * kg) | 3 | cm³/10min | ISO 1133 |
Regulatory & Compliance
- Certifications & Compliance
- OEM Specifications
- OEM Standards
- Quality Standards
Technical Details & Test Data
- Chemical Resistance
Chemical Type Chemical Name Resistance Other Acetic acid (10% by mass) at 23°C resistant Ketones Acetone at 23°C resistant Other Ammonium hydroxide (10% by mass) at 23°C limited resistant, tests necessary to verify Other ASTM 1 at 23°C resistant Other ASTM 3 at 23°C resistant Other Brake fluids (DOT 3/4) at 23°C not resistant Other Calcium chloride (10% by mass) at 23°C limited resistant, tests necessary to verify Other Chloroform at 23°C not resistant Ethers Diethyl ether at 23°C limited resistant, tests necessary to verify Alcohols Ethanol at 23°C limited resistant, tests necessary to verify Other Ethyl Acetate at 23°C limited resistant, tests necessary to verify Other Fuel; Diesel at 85°C resistant Other Hydrochloric acid (10% by mass) at 23°C resistant Other Hydrogen peroxide (30% by mass) at 23°C limited resistant, tests necessary to verify Other Nitric acid (10% by mass) at 23°C resistant Other Phosphoric acid (10% by mass) at 23°C resistant Other Sodium hydroxide (10% by mass) at 23°C resistant Other Sulfuric acid (30% by mass) at 23°C resistant Other Tetrachloroethylene at 23°C limited resistant, tests necessary to verify Hydrocarbons Toluene at 23°C resistant Other Transformer oil at 23°C not resistant Other Trichloroethylene at 23°C not resistant Other Water at 23°C resistant Other Zinc chloride (10% by mass) at 23°C resistant - Dynamic Tensile Modulus (E)-Temperature
- Stress-Strain
- Stress-Strain (TPE)