Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Mechanical Properties
- Thermal Properties
- Other Properties
- Mechanical Properties (Die Cutting)
- Mechanical Properties (TPE)
- Rheological Properties
| Value | Units | Test Method / Conditions | |
| Flexural Modulus | 310 | MPa | ISO 178 |
| Flexural Modulus (at 120°C) | 110 | MPa | ISO 178 |
| Charpy Impact Strength (at 23°C) | N | kJ/m² | ISO 179/1eU |
| Charpy Impact Strength (at -30°C) | N | kJ/m² | ISO 179/1eU |
| Charpy Notched Impact Strength (at 23°C) | N | kJ/m² | ISO 179/1eA |
| Charpy Notched Impact Strength (at -30°C) | 15 | kJ/m² | ISO 179/1eA |
| Izod Notched Impact Strength (at 23°C) | N | kJ/m² | ISO 180/1A |
| Value | Units | Test Method / Conditions | |
| Temperature of Deflection Under Load (at 0.45 MPa) | 100 | °C | ISO 75-1/-2 |
| Melting Temperature (at 10°C/min) | 220 | °C | ISO 11357-1/-3 |
| Vicat Softening Temperature (at 50°C/h 50N) | 105 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Density | 1230 | kg/m³ | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Stress (at Break, Normal) | 41 | MPa | ISO 527-1/-2 |
| Stress (at 5% Strain, Normal) | 11 | MPa | ISO 527-1/-2 |
| Stress (at 10% Strain, Normal) | 15 | MPa | ISO 527-1/-2 |
| Stress (at 50% Strain, Normal) | 17.5 | MPa | ISO 527-1/-2 |
| Stress (at 10% Strain, Parallel, 100°C) | 7.1 | MPa | ISO 527-1/-2 |
| Stress (at 100% Strain, Normal) | 17 | MPa | ISO 527-1/-2 |
| Strain (at Break, Normal) | 610 | % | ISO 527-1/-2 |
| Stress (at 10% Strain, Parallel) | 14 | MPa | ISO 527-1/-2 |
| Tear Strength (Normal) | 131 | kN/m | ISO 34-1; Method B |
| Tear Strength (Parallel) | 137 | kN/m | ISO 34-1; Method B |
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 300 | MPa | ISO 527-1/-2 |
| Stress (at 5% Strain) | 13 | MPa | ISO 527-1/-2 |
| Stress (at 10% Strain) | 18 | MPa | ISO 527-1/-2 |
| Stress (at 50% Strain) | 25 | MPa | ISO 527-1/-2 |
| Stress (at 100% Strain) | 28 | MPa | ISO 527-1/-2 |
| Stress (at Break) | 30 | MPa | ISO 527-1/-2 |
| Nominal Strain (at Break) | 150 | % | ISO 527-1/-2 |
| Hardness (3s) | 55 | Shore D | ISO 868 |
| Value | Units | Test Method / Conditions | |
| Melt Volume Flow Rate (at 230°C, 10 kg) | 2.9 | cm³/10min | ISO 1133 |
Regulatory & Compliance
- Certifications & Compliance
- OEM Specifications
- OEM Standards
Technical Details & Test Data
- Stress Strain (TPE)
- Chemical Resistance Data
Chemical Name Chemical Resitance Acetic acid (10% by mass) at 23°C Resistant Acetone at 23°C Resistant Ammonium hydroxide (10% by mass) at 23°C Limited resistant, tests necessary to verify
ASTM 1 at 23°C Resistant ASTM 3 at 23°C Resistant Brake fluids (DOT 3/4) at 23°C Not resistant Calcium chloride (10% by mass) at 23°C Limited resistant, tests necessary to verify
Chloroform at 23°C Not resistant Diethyl ether at 23°C Limited resistant, tests necessary to verify
Ethanol at 23°C Limited resistant, tests necessary to verify
Ethyl Acetate at 23°C Limited resistant, tests necessary to verify
Fuel; Diesel at 85°C Resistant Hydrochloric acid (10% by mass) at 23°C Resistant Hydrogen peroxide (30% by mass) at 23°C Limited resistant, tests necessary to verify
Nitric acid (10% by mass) at 23°C Resistant Phosphoric acid (10% by mass) at 23°C Resistant Sodium hydroxide (10% by mass) at 23°C Resistant Sulfuric acid (30% by mass) at 23°C Resistant Tetrachloroethylene at 23°C Limited resistant, tests necessary to verify
Toluene at 23°C Resistant Transformer oil at 23°C Not resistant Trichloroethylene at 23°C Not resistant Water at 23°C Resistant Zinc chloride (10% by mass) at 23°C Resistant - Dynamic Tensile Modulus (E) Temperature
Packaging & Availability